Structural and Magnetic Properties of Cr3+ Doped Mg Ferrites
Open Access
- 1 January 2012
- journal article
- Published by Scientific Research Publishing, Inc. in World Journal of Condensed Matter Physics
- Vol. 02 (01), 27-35
- https://doi.org/10.4236/wjcmp.2012.21005
Abstract
The polycrystalline MgCrxFe2-xO4 ferrites (0.0 ? x ? 1.0) were prepared by conventional solid state ceramic sintering technique in air at 1300?C. X-ray diffraction experiments were carried out on all the samples in order to characterize the materials at room temperature. The X-ray diffraction patterns showed sharp peaks indicating the formation of single phased cubic spinel structure. The lattice parameters of the samples were determined from the X-ray diffraction data using Nelson-Riley extrapolation method. It was found that the lattice parameter decreased with increasing Cr concen- tration obeying Vegard’s law. Magnetic properties of the samples were measured using an Impedance Analyzer. Real and imaginary parts of the complex permeability, loss factor and quality factor were measured as the function of frequency at three different sintering temperatures 1250?C, 1300?C and 1350?C for all the samples in the frequency range 1 kHz to 13 MHz. Frequency stability of the real part of permeability increases with increasing Cr concentration and also with sintering temperature. Imaginary part of permeability decreases with increasing frequency and increased with increasing both of the Cr content and sintering temperature. Loss factor decreased with increasing frequency while the quality factor (Q) increased with increasing frequency for all the samples. The temperature de- pendence of initial permeability was measured for all the samples sintered at 1300?C. The Curie temperature (Tc) was determined from the -T curves. The values of Tc were found to be 733 K, 657 K, 583 K, 468 K, 400 K and 317 K for x = 0.0, 0.2, 0.4, 0.6, 0.8 and 1.0, respectively.Keywords
This publication has 23 references indexed in Scilit:
- Crystallographic and magnetic properties of the spinel type solid solution Zn0.4Co0.6AlxFe2$minus;xO4 (0$le;x$le;1)Materials Research Bulletin, 2004
- Electrical Properties of Co-Zn Ferritesphysica status solidi (a), 1989
- Resonance and Relaxation of Domain Walls in Polycrystalline Ferritesphysica status solidi (a), 1983
- Dielectric behaviour of mixed Li-Ni ferrites at low frequenciesJournal of the Less Common Metals, 1982
- The causes of the anomalous loss in amorphous ribbon materialsIEEE Transactions on Magnetics, 1981
- An apparatus for the measurement of initial magnetic permeability as a function of temperatureJournal of Physics E: Scientific Instruments, 1980
- Determination of initial magnetization curve from crystallites size and effective anisotropy fieldIEEE Transactions on Magnetics, 1971
- The Néel Theory of FerrimagnetismAmerican Journal of Physics, 1955
- Dimensional Effects Resulting from a High Dielectric Constant Found in a Ferromagnetic FerritePhysical Review B, 1950
- Die Konstitution der Mischkristalle und die Raumf llung der AtomeThe European Physical Journal A, 1921