A General Approach to Preferential Formation of Active Fe–Nx Sites in Fe–N/C Electrocatalysts for Efficient Oxygen Reduction Reaction
Top Cited Papers
- 1 November 2016
- journal article
- research article
- Published by American Chemical Society (ACS) in Journal of the American Chemical Society
- Vol. 138 (45), 15046-15056
- https://doi.org/10.1021/jacs.6b09470
Abstract
Iron–nitrogen on carbon (Fe–N/C) catalysts have emerged as promising nonprecious metal catalysts (NPMCs) for oxygen reduction reaction (ORR) in energy conversion and storage devices. It has been widely suggested that an active site structure for Fe–N/C catalysts contains Fe–Nx coordination. However, the preparation of high-performance Fe–N/C catalysts mostly involves a high-temperature pyrolysis step, which generates not only catalytically active Fe–Nx sites, but also less active large iron-based particles. Herein, we report a general “silica-protective-layer-assisted” approach that can preferentially generate the catalytically active Fe–Nx sites in Fe–N/C catalysts while suppressing the formation of large Fe-based particles. The catalyst preparation consisted of an adsorption of iron porphyrin precursor on carbon nanotube (CNT), silica layer overcoating, high-temperature pyrolysis, and silica layer etching, which yielded CNTs coated with thin layer of porphyrinic carbon (CNT/PC) catalysts. Temperature-controlled in situ X-ray absorption spectroscopy during the preparation of CNT/PC catalyst revealed the coordination of silica layer to stabilize the Fe–N4 sites. The CNT/PC catalyst contained higher density of active Fe–Nx sites compared to the CNT/PC prepared without silica coating. The CNT/PC showed very high ORR activity and excellent stability in alkaline media. Importantly, an alkaline anion exchange membrane fuel cell (AEMFC) with a CNT/PC-based cathode exhibited record high current and power densities among NPMC-based AEMFCs. In addition, a CNT/PC-based cathode exhibited a high volumetric current density of 320 A cm–3 in acidic proton exchange membrane fuel cell. We further demonstrated the generality of this synthetic strategy to other carbon supports.Keywords
Funding Information
- National Research Foundation of Korea (NRF-2013H1A2A1032644, NRF-2014R1A2A1A05002488, NRF-2015M1A2A2056560)
- Korea Evaluation Institute of Industrial Technology (10050509)
This publication has 83 references indexed in Scilit:
- Nanostructured electrocatalysts with tunable activity and selectivityNature Reviews Materials, 2016
- Recent Advances in Electrocatalysts for Oxygen Reduction ReactionChemical Reviews, 2016
- Earth‐Abundant Nanomaterials for Oxygen ReductionAngewandte Chemie-International Edition, 2015
- Electrochemical Energy Engineering: A New Frontier of Chemical Engineering InnovationAnnual Review of Chemical and Biomolecular Engineering, 2014
- Electrocatalysts for Alkaline Polymer Exchange Membrane (PEM) Fuel Cells – OverviewPublished by Wiley ,2014
- Electrocatalyst approaches and challenges for automotive fuel cellsNature, 2012
- Recent advances in non-precious metal catalysis for oxygen-reduction reaction in polymer electrolyte fuelcellsEnergy & Environmental Science, 2010
- Progress in the synthesis of carbon nanotube- and nanofiber-supported Pt electrocatalysts for PEM fuel cell catalysisJournal of Applied Electrochemistry, 2006
- Activity benchmarks and requirements for Pt, Pt-alloy, and non-Pt oxygen reduction catalysts for PEMFCsApplied Catalysis B: Environment and Energy, 2004
- Materials for fuel-cell technologiesNature, 2001