Structural evolution and adhesion of titanium oxide film containing phosphorus and calcium on titanium by anodic oxidation
- 9 August 2007
- journal article
- research article
- Published by Wiley in Journal of Biomedical Materials Research Part A
- Vol. 85A (2), 378-387
- https://doi.org/10.1002/jbm.a.31510
Abstract
This study investigated the microstructure evolution and defects of the titanium oxide layer containing calcium (Ca) and phosphorus (P) formed by anodic oxidation in a solution containing Ca and P compounds. Results show that the anodic film exhibited a two-layer structure: a pore-containing amorphous titanium oxide layer dispersed with nano-sized crystallites formed prior to sparking, and a porous overlay dotted with craters formed after sparking. Ca and P were predominantly incorporated in the porous overlay, in which the amorphous region contained more Ca and P than the crystalline region regardless of the anodizing voltages. Moreover, the ratio of amorphous to crystalline regions in the porous overlay changed insignificantly with anodizing voltage. Increasing anodizing voltage enhanced the incorporation of Ca and P in the anodic film, but deteriorated the adhesion of the anodic film to the substrate. This deterioration was related to two inherent adhesive weaknesses: the aligned pores in the titanium oxide layer and the craters in the major overlay, signifying that a new anodic oxidation process that can produce high Ca- and P-containing oxide film at relatively-low anodizing voltages, i.e. ∼200 V, is a necessity. © 2007 Wiley Periodicals, Inc. J Biomed Mater Res, 2008Keywords
This publication has 32 references indexed in Scilit:
- Biocompatibility of titanium implants modified by microarc oxidation and hydroxyapatite coatingJournal of Biomedical Materials Research Part A, 2005
- Analysis of In-Vitro Reaction Layers Formed on Plasma Sprayed Bioglass-Titanium CoatingsKey Engineering Materials, 2004
- The modulation of osteogenesis in vitro by calcium titanium phosphate coatingsBiomaterials, 2004
- Biomimetic apatite coatings on micro-arc oxidized titaniaBiomaterials, 2003
- In vitro osteoblast response to anodized titanium and anodized titanium followed by hydrothermal treatmentJournal of Biomedical Materials Research Part A, 2003
- Biological performance of biomimetic calcium phosphate coating of titanium implants in the dog mandibleJournal of Biomedical Materials Research Part A, 2002
- Mechanical and histological investigation of hydrothermally treated and untreated anodic titanium oxide films containing Ca and PJournal of Biomedical Materials Research, 1995
- Formation and characterization of anodic titanium oxide films containing Ca and PJournal of Biomedical Materials Research, 1995
- Structure and integrity of a plasma sprayed hydroxylapatite coating on titaniumJournal of Biomedical Materials Research, 1993
- Interface between bone tissue and implants of solid hydroxyapatite or hydroxyapatite-coated titanium implantsBiomaterials, 1989