Self-Compacting Concrete Reinforced with Twisted-Bundle Macro-Synthetic Fiber

Abstract

The use of self-compacting concrete (SCC) reinforced with fibers has great potential in the precast concrete industry as the concrete can be delivered straight into the moulds, without any vibration or compacting effort. Similarly, it has the potential to replace traditional steel reinforcement depending on the design requirements. Novel synthetic fibers have recently become available in the market, but still, limited information is available on the performance of SCC reinforced with such fibers. This paper investigates the use of twisted-bundle macro-synthetic fiber in self-compacting concrete. Three different concrete mixtures with fiber dosage of 4, 6, and 8 kg/m³ were produced in large scale batches, and their performance was compared in terms of slump-flow, compressive strength, split tensile strength, modulus of elasticity, and flexural strength. Moreover, a comprehensive evaluation of the post-cracking residual strength is presented. It was found that the mixture with 4 kg/m³ fiber content has the most satisfactory flowability, whereas 8 kg/m³ mixture achieved the highest residual flexural strength. Based on the observed post-cracking behavior, a simplified stress-crack opening constitutive law is proposed. Since the fiber dosage affects the residual flexural strength, a factor related to fiber content is recommended while determining the ultimate residual flexural strength.