Plating and stripping calcium in an organic electrolyte
- 31 December 2017
- journal article
- research article
- Published by Springer Science and Business Media LLC in Nature Materials
- Vol. 17 (1), 16-20
- https://doi.org/10.1038/NMAT5036
Abstract
There is considerable interest in multivalent cation batteries, such as those based on magnesium, calcium or aluminium(1-11). Most attention has focused on magnesium. In all cases the metal anode represents a significant challenge. Recent work has shown that calcium can be plated and stripped, but only at elevated temperatures, 75 to 100 degrees C, with small capacities, typically 0.165 mAh cm(-2), and accompanied by significant side reactions(7). Here we demonstrate that calcium can be plated and stripped at room temperature with capacities of 1 mAh cm(-2) at a rate of 1 mA cm(-2), with low polarization (similar to 100 mV) and in excess of 50 cycles. The dominant product is calcium, accompanied by a small amount of CaH2 that forms by reaction between the deposited calcium and the electrolyte, Ca(BH4)(2) in tetrahydrofuran (THF). This occurs in preference to the reactions which take place in most electrolyte solutions forming CaCO3, Ca(OH)(2) and calcium alkoxides, and normally terminate the electrochemistry. The CaH2 protects the calcium metal at open circuit. Although this work does not solve all the problems of calcium as an anode in calcium-ion batteries, it does demonstrate that significant quantities of calcium can be plated and stripped at room temperature with lowpolarization.Keywords
This publication has 29 references indexed in Scilit:
- Theoretical Analysis of Interactions between Potassium Ions and Organic Electrolyte Solvents: A Comparison with Lithium, Sodium, and Magnesium IonsJournal of the Electrochemical Society, 2016
- High-capacity zinc-ion storage in an open-tunnel oxide for aqueous and nonaqueous Zn-ion batteriesJournal of Materials Chemistry A, 2016
- Towards a calcium-based rechargeable batteryNature Materials, 2015
- Reversible Multivalent (Monovalent, Divalent, Trivalent) Ion Insertion in Open Framework MaterialsAdvanced Energy Materials, 2015
- An ultrafast rechargeable aluminium-ion batteryNature, 2015
- Quest for Nonaqueous Multivalent Secondary Batteries: Magnesium and BeyondChemical Reviews, 2014
- Mg rechargeable batteries: an on-going challengeEnergy & Environmental Science, 2013
- Electrolyte roadblocks to a magnesium rechargeable batteryEnergy & Environmental Science, 2012
- Electrochemical characteristics of calcium in organic electrolyte solutions and vanadium oxides as calcium hostsJournal of Power Sources, 2003
- Prototype systems for rechargeable magnesium batteriesNature, 2000