Influence of surface area and additives on the thermal stability of transition alumina catalyst supports. I: Kinetic data
- 1 January 1987
- journal article
- Published by Elsevier BV in Applied Catalysis
- Vol. 34, 225-238
- https://doi.org/10.1016/s0166-9834(00)82458-6
Abstract
The influence of surface area and additives on the transformation of transition aluminas into alpha alumina was studied using differential thermal analysis and by measuring the rate of transformation by X-ray diffraction of samples calcined at numerous intervals during a 50 hour period. Four transition alumina samples of different specific surface area ranging from 80 to 130 m2 g−1 were used. The transformation was found to be facilitated by a high surface area of the initial transition alumina. Initially the surface area decreased very rapidly from its starting value until about 60 m2 g−1 then more slowly and also linearly with respect to the amount of alpha phase in the sample. The influence of additives was followed by adding Mg2+, Ca2+, Ga3+, In3+, La3+, Zr4+ and Th4+ cations by the dry impregnation method with nitrate salts. The influence of the method of preparation was determined by using the same procedure for aluminium nitrate. By comparison with pure alumina and in order of increasing effect. In3+, Ga3+, Al3+ and Mg2+ were found to be accelerators, whereas Zr4+, Ca2+, Th4+ and La3+ were found to be inhibitors. The influence of adding an ion to different initial aluminas was investigated in the case of Mg2+.Keywords
This publication has 9 references indexed in Scilit:
- A shear-type allotropie transformation in aluminaMetallurgical Transactions B, 1985
- The influence of lanthanum oxide on the thermal stability of gamma alumina catalyst supportsApplied Catalysis, 1983
- The effect of Cr3+ and Fe3+ ions on the transformation of different aluminum hydroxides to α-Al2O3Thermochimica Acta, 1983
- The γ→α Phase Transformation in Al2O3MRS Proceedings, 1983
- Metastable Phases of AluminaMRS Proceedings, 1983
- Influence of Cr and Fe on Formation of α‐Al2O3 from γ‐Al2O3Journal of the American Ceramic Society, 1974
- Kinetics of the Gamma-to-Alpha Alumina Phase TransformationJournal of the American Ceramic Society, 1971
- The Role of Water Vapor in Formation of Alpha Alumina from Transient AluminaJournal of the Ceramic Association, Japan, 1966
- High Temperature Changes in Alumina Structure and Activity of Platinum-Alumina CatalystsIndustrial & Engineering Chemistry, 1960