Tuned Polymer Electrolyte Membranes Based on Aromatic Polyethers for Fuel Cell Applications
- 13 March 2007
- journal article
- research article
- Published by American Chemical Society (ACS) in Journal of the American Chemical Society
- Vol. 129 (13), 3879-3887
- https://doi.org/10.1021/ja0672526
Abstract
Poly(arylene ether sulfone)-based ionomers containing sulfofluorenyl groups have been synthesized for applications to polymer electrolyte membrane fuel cells (PEMFCs). In order to achieve high proton conductivity and chemical, mechanical, and dimensional stability, the molecular structure of the ionomers has been optimized. Tough, flexible, and transparent membranes were obtained from a series of modified ionomers containing methyl groups with the ion-exchange capacity (IEC) ranging from 1.32 to 3.26 meq/g. Isopropylidene tetramethylbiphenylene moieties were more effective than the methyl-substituted fluorenyl groups in giving a high-IEC ionomer membrane with substantial stability to hydrolysis and oxidation. Dimensional stability was significantly improved for the methyl-substituted ionomer membranes compared to that of the non-methylated ones. This new ionomer membrane showed comparable proton conductivity to that of the perfluorinated ionomer membrane (Nafion 112) under a wide range of conditions (80−120 °C and 20−93% relative humidity (RH)). The highest proton conductivity of 0.3 S/cm was obtained at 80 °C and 93% RH. Although there is a decline of proton conductivity with time, after 10 000 h the proton conductivities were still at acceptable levels for fuel cell operation. The membranes retained their strength, flexibility, and high molecular weight after 10 000 h. Microscopic analyses revealed well-connected ionic clusters for the high-IEC membrane. A fuel cell operated using the polyether ionomer membrane showed better performance than that of Nafion at a low humidity of 20% RH and high temperature of 90 °C. Unlike the other hydrocarbon ionomers, the present membrane showed a lower resistance than expected from its conductivity, indicating superior water-holding capability at high temperature and low humidity.Keywords
This publication has 36 references indexed in Scilit:
- Emerging membrane materials for high temperature polymer electrolyte fuel cells: durable hydrocarbon ionomersJournal of Materials Chemistry, 2006
- Molded, High Surface Area Polymer Electrolyte Membranes from Cured Liquid PrecursorsJournal of the American Chemical Society, 2006
- Fluorenyl-containing sulfonated poly(aryl ether ether ketone ketone)s (SPFEEKK) for fuel cell applicationsJournal of Membrane Science, 2006
- DFT investigation of the polymer electrolyte membrane degradation caused by OH radicals in fuel cellsJournal of Membrane Science, 2006
- Poly(phthalazinone ether ketone) Ionomers Synthesized via N−C Coupling Reaction for Fuel Cell ApplicationsMacromolecules, 2005
- Novel Synthesis of Sulfonated Poly(phthalazinone ether ketone) Used as a Proton Exchange Membrane via N−C Coupling ReactionMacromolecules, 2005
- Synthesis of Polyphosphazenes with Sulfonimide Side GroupsMacromolecules, 2002
- Synthesis and Properties of Novel Sulfonated Arylene Ether/Fluorinated Alkane CopolymersMacromolecules, 2001
- Synthesis, characterization and evaluation of new fluorene-based dimethacrylates for formulating dental compositesPolymers for Advanced Technologies, 1999
- New synthesis of poly(arylene ether)s using masked bisphenolsJournal of the Chemical Society, Chemical Communications, 1991