Mechano-Active Scaffold Design Based on Microporous Poly(L-lactide-co-ε-caprolactone) for Articular Cartilage Tissue Engineering: Dependence of Porosity on Compression Force-Applied Mechanical Behaviors
- 1 March 2006
- journal article
- research article
- Published by Mary Ann Liebert Inc in Tissue Engineering
- Vol. 12 (3), 449-458
- https://doi.org/10.1089/ten.2006.12.449
Abstract
An essential component of functional articular cartilage tissue engineering is a mechano-active scaffold, which responds to applied compression stress and causes little permanent deformation. As the first paper of a series on mechano-active scaffold-based cartilage tissue engineering, this study focused on mechanical responses to various modes of loading of compression forces and subsequent selection of mechano-active scaffolds from the biomechanical viewpoint. Scaffolds made of elastomeric microporous poly(L-lactide-co-ε-caprolactone) (PLCL) with open-cell structured pores (300 ∼ 500 µm) and with different porosities ranging from 71 to 86% were used. The PLCL sponges and rabbit articular cartilage tissue were subjected to compression/unloading tests (0.1 and 0.005 Hz) at 5 kPa, and stress relaxation tests at 10, 30, and 50% strain. The measurements of the maximum strain under loading and residual strain under unloading for compression tests and the maximum stress and equilibrium stress in the stress relaxation test showed that the lower the porosity, the closer the mechanical properties are to those of native cartilage tissue. Among the PLCL sponges, the sponge with 71% porosity appears to be a suitable cartilage scaffold.Keywords
This publication has 18 references indexed in Scilit:
- Morphology of Elastic Poly(l-lactide-co-ε-caprolactone) Copolymers and in Vitro and in Vivo Degradation Behavior of Their ScaffoldsBiomacromolecules, 2004
- Synthesis of biodegradable poly(propylene fumarate) networks with poly(propylene fumarate)–diacrylate macromers as crosslinking agents and characterization of their degradation productsPolymer, 2001
- Fibroblast culture on surface-modified poly (glycolide-co-ε-caprolactone) scaffold for soft tissue regenerationJournal of Biomaterials Science, Polymer Edition, 2001
- Review: tissue engineering for regeneration of articular cartilageBiomaterials, 2000
- Meniscal tissue regeneration in porous 50/50 copoly(l-lactide/ε-caprolactone) implantsBiomaterials, 1997
- Biological performance of a degradable poly(lactic acid‐ε‐caprolactone) nerve guide: Influence of tube dimensionsJournal of Biomedical Materials Research, 1995
- Polylactones: 31. Sn(II)octoate-initiated polymerization of L-lactide: a mechanistic studyPolymer, 1995
- Biodegradable Polymer Scaffolds for Tissue EngineeringNature Biotechnology, 1994
- (Co)polymers of L‐lactide, 2. Mechanical propertiesMacromolecular Chemistry and Physics, 1994
- High molecular weight copolymers of l-lactide and ?-caprolactone as biodegradable elastomeric implant materialsPolymer Bulletin, 1991