INITIAL GROWTH PROCESS OF MAGNETRON SPUTTERING 321 STAINLESS STEEL FILMS OBSERVED BY AFM
- 1 December 2007
- journal article
- Published by World Scientific Pub Co Pte Ltd in Surface Review and Letters
- Vol. 14 (6), 1053-1059
- https://doi.org/10.1142/s0218625x07010627
Abstract
To investigate the initial morphological evolution of 321 stainless steel (SS) films, we examined the effect of sputtering time on the morphology of 321 SS film. In this study, a group of samples were prepared at nine different sputtering times within 20 s using radio-frequency (r.f.) magnetron sputtering and characterized by atomic force microscopy (AFM). Only globular-like grains were formed on mica substrates within 6 s, whose average grain size is ~ 21–44 nm. Meanwhile, few grains with larger size are subject to settle at the defect sites of mica substrates. At 8 s, we found large columnar crystallites with the average grain size of 61 nm. From 10 to 14 s, islands grew continuously and coalesced in order to form an interconnected structure containing irregular channels or grooves, with a depth of ~ 3.5–5 nm. Up to 16 s, a nearly continuous film was formed and some new globular-like grains were again present on the film. Study of the AFM image at 20 s suggests that the watercolor masking method designed by us is an effective method, by which we can prepare thin films with steps for the measurement of the thickness of continuous thin films. It is also found that the coverage rate of films increases with the increase in sputtering time (from 2 to 16 s). On the other hand, the increase in root mean square (RMS) roughness is much more significant from 6 to 10 s, and there is a maximum value, 2.81 nm at 10 s due to more islands during deposition. However, RMS roughness decreases with the decrease in length and width of channels or grooves from 10 to 16 s. Especially, a lower RMS roughness of 0.73 nm occurs at 16 s, because of the continuous film produced with a large coverage rate of 98.43%.Keywords
This publication has 7 references indexed in Scilit:
- Growth and characterization of tin disulfide (SnS2) thin film deposited by successive ionic layer adsorption and reaction (SILAR) techniqueJournal of Alloys and Compounds, 2007
- Surface and nanoindentation studies on nanocrystalline titanium diboride thin film deposited by magnetron sputteringThin Solid Films, 2007
- Fatigue strength of small-scale type 304 stainless steel thin filmsMaterials Science and Engineering: A, 2006
- Formation of β-C3N4 grains by sputteringSurface Engineering, 2000
- Studies using AFM and STM of the correlated effects of the deposition parameters on the topography of gold on micaThin Solid Films, 1997
- STM study of the surface morphology of gold on micaSurface Science, 1988
- Atomic Force MicroscopePhysical Review Letters, 1986