Influence of organic acids present in the oral biofilm on the microtensile bond strength of adhesive systems to human dentin
- 21 December 2011
- journal article
- research article
- Published by Wiley in Journal of Biomedical Materials Research Part B: Applied Biomaterials
- Vol. 100B (3), 735-741
- https://doi.org/10.1002/jbm.b.32506
Abstract
This study evaluated the influence of organic acids present in the oral biofilm on the microtensile bond strength (μTBS) of adhesive systems to human dentin. Sixty occlusal dentin surfaces were wet ground with 600 grit SiC abrasive paper and divided into four groups according to the adhesive systems: Scotchbond Multipurpose (SMP), Adper Single Bond 2, Adper Scotchbond SE (ASE), and Clearfill SE Bond (CSE). After the adhesive systems were applied, a block of resin composite was built up on the dentin surfaces. After 24 h storage in distilled water at 37°C, the teeth were perpendicularly cut to obtain beams (1 mm2). For each adhesive system, the beams were divided into three groups according to storage media: artificial saliva (AS); propionic acid (PA), and lactic acid (LA). After 7 days storage at 37°C, the beams were submitted to μTBS testing. The μTBS ranged from 36.0 ± 1.6 (ASE‐PA) to 52.5 ± 1.2 (CSE‐AS). For all adhesive systems, the μTBS values after storage in PA were lower than those in AS. Except for the SMP, the values of μTBS after storage in LA were lower than those in AS. The adhesive ASE presented the lowest values of μTBs in the three media. The acids present in the oral biofilm may affect the bond strength of adhesive systems to human dentin. © 2011 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2012.Keywords
This publication has 40 references indexed in Scilit:
- Six-month evaluation of adhesives interface created by a hydrophobic adhesive to acid-etched ethanol-wet bonded dentine with simplified dehydration protocolsJournal of Dentistry, 2010
- Three-year clinical evaluation of a flowable and a hybrid resin composite in non-carious cervical lesionsJournal of Dentistry, 2010
- Analysis of differential artificial ageing of the adhesive interface produced by a two‐step etch‐and‐rinse adhesiveEuropean Journal of Oral Sciences, 2009
- Reinforcement of dentin in self-etch adhesive technology: A new conceptJournal of Dentistry, 2009
- Effect of Operator-specific Handling on Tooth-composite Interface and Microleakage FormationOperative Dentistry, 2009
- Four-year water degradation of a total-etch and two self-etching adhesives bonded to dentinJournal of Dentistry, 2008
- Can the durability of one-step self-etch adhesives be improved by double application or by an extra layer of hydrophobic resin?Journal of Dentistry, 2008
- Resistance of ten contemporary adhesives to resin–dentine bond degradationJournal of Dentistry, 2008
- Bonding characteristics of newly developed all‐in‐one adhesivesJournal of Biomedical Materials Research Part B: Applied Biomaterials, 2006
- Softening of BISGMA‐based polymers by ethanol and by organic acids of plaqueEuropean Journal of Oral Sciences, 1984