State-of-the-Art and Practical Guide to Ultrasonic Transducers for Harsh Environments Including Temperatures above 2120 °F (1000 °C) and Neutron Flux above 1013 n/cm2
Open Access
- 1 November 2019
- Vol. 19 (21), 4755
- https://doi.org/10.3390/s19214755
Abstract
In field applications currently used for health monitoring and nondestructive testing, ultrasonic transducers primarily employ PZT5-H as the piezoelectric element for ultrasound transmission and detection. This material has a Curie–Weiss temperature that limits its use to about 210 °C. Some industrial applications require much higher temperatures, i.e., 1000–1200 °C and possible nuclear radiation up to 1020 n/cm2 when performance is required in a reactor environment. The goal of this paper is the survey and review of piezoelectric elements for use in harsh environments for the ultimate purpose for structural health monitoring (SHM), non-destructive evaluation (NDE) and material characterization (NDMC). The survey comprises the following categories: 1. High-temperature applications with single crystals, thick-film ceramics, and composite ceramics, 2. Radiation-tolerant materials, and 3. Spray-on transducers for harsh-environment applications. In each category the known characteristics are listed, and examples are given of performance in harsh environments. Highlighting some examples, the performance of single-crystal lithium niobate wafers is demonstrated up to 1100 °C. The wafers with the C-direction normal to the wafer plane were mounted on steel cylinders with high-temperature Sauereisen and silver paste wire mountings and tested in air. In another example, the practical use in harsh radiation environments aluminum nitride (AlN) was found to be a good candidate operating well in two different nuclear reactors. The radiation hardness of AlN was evident from the unaltered piezoelectric coefficient after a fast and thermal neutron exposure in a nuclear reactor core (thermal flux = 2.12 × 1013 ncm−2; fast flux 2 (>1.0 MeV) = 4.05 × 1013 ncm−2; gamma dose rate: 1 × 109 r/h; temperature: 400–500 °C). Additionally, some of the high-temperature transducers are shown to be capable of mounting without requiring coupling material. Pulse-echo signal amplitudes (peak-to-peak) for the first two reflections as a function of the temperature for lithium niobate thick-film, spray-on transducers were observed to temperatures of about 900 °C. Guided-wave send-and-receive operation in the 2–4 MHz range was demonstrated on 2–3 mm thick Aluminum (6061) structures for possible field deployable applications where standard ultrasonic coupling media do not survive because of the harsh environment. This approach would benefit steam generators and steam pipes where temperatures are above 210 °C. In summary, there are several promising approaches to ultrasonic transducers for harsh environments and this paper presents a survey based on literature searches and in-house laboratory observations.Keywords
This publication has 48 references indexed in Scilit:
- High temperature ultrasonic transducer up to 1000 °C using lithium niobate single crystalApplied Physics Letters, 2010
- Effect of neutron irradiation on some piezoelectric properties of PZT type ceramicsJournal de Physique IV, 2005
- Ion-induced amorphization in ceramic materialsJournal of Nuclear Materials, 2005
- Neutron irradiation effects on isotope tailored aluminum nitride ceramics by a fast reactor up to 2×l026 n/m2Journal of Nuclear Materials, 2004
- Amorphization and recrystallization of the ABO3 oxidesJournal of Nuclear Materials, 2002
- Radiation effects in ceramicsJournal of Nuclear Materials, 1994
- Studying the electrophysical parameters of piezoceramics of various types in an IVV-2M reactorAtomic Energy, 1984
- Durability of ZTL piezoceramic under the action of reactor radiationAtomic Energy, 1982
- The effect of low-fluence neutron irradiation on silver-electroded lead-zirconate-titanate piezoelectric ceramicsJournal of Nuclear Materials, 1980
- Effects of Radiation‐Induced Damage Centers in Lead Zirconate Titanate CeramicsJournal of the American Ceramic Society, 1965