Origins of the elastic behavior of nanoparticle chain aggregates: Measurements using nanostructure manipulation device
- 15 March 2003
- journal article
- research article
- Published by AIP Publishing in Journal of Applied Physics
- Vol. 93 (6), 3515-3523
- https://doi.org/10.1063/1.1542924
Abstract
Nanoscale studies were conducted on the dynamic behavior of individual nanoparticle chain aggregates (NCAs) and their networks. For this purpose, device was fabricated to apply tension to NCA under controlled conditions. The device is composed of a specimen support and a cartridge. The specimen support is a deformable alloy disk with a narrow slit across which the NCAs are deposited; the cartridge is used to connect the specimen support to a specimen elongation support holder. The aggregates were stretched using the specimen holder to widen or narrow the slit gap at speeds from 0.5 to 300 nm/s and the motion was observed with a transmission electron microscope. Most of the studies were made with carbon NCA (primary particle size between 11 and 16 nm) generated by laser ablation of a graphite target. The aggregates were deposited on the specimen support (disk) to form bridges across the slit. When tension was applied, the NCA chains remained attached at the slit edges; the chains stretched as kinks on the scale of a few particle diameters were straightened by rotation and/or grain boundary sliding at particle–particle interfaces. After the chain became taut, increasing tension produced little additional extension. Eventually, the chain broke, the tension relaxed, and the elastically strained portions along the NCA recovered. This led to fast contraction of the two broken ends. In one of the cases studied in detail, a small primary particle in the chain doubled in length before the chain broke at this site. This probably occurred because of the high tensile stress in the small particle. In separate experiments, a network of carbon NCA was produced by increased deposition around the slit of a specimen support. Chains in the network broke successively as the network stretched. Some of the chains broke midway and not at the junctures with each other. They contracted fast showing behavior similar to that of the individual aggregates. Possible applications to the behavior of nanocomposite materials composed of blends of NCAs and molecular polymers (e.g., rubber) are described.Keywords
This publication has 18 references indexed in Scilit:
- Elastic properties of nanoparticle chain aggregates of TiO2, Al2O3, and Fe2O3 generated by laser ablationJournal of Applied Physics, 2000
- The Role of Filler Networking in Dynamic Properties of Filled RubberRubber Chemistry and Technology, 1999
- Elastic behavior of nanoparticle chain aggregatesApplied Physics Letters, 1998
- Effects of Dispersion and Aggregation of Silica in the Reinforcement of Poly(methyl acrylate) ElastomersChemistry of Materials, 1997
- Tear Strength of Carbon-Black-Filled CompoundsRubber Chemistry and Technology, 1996
- Threshold tensile strength and modulus of carbon-black-filled rubber vulcanizatesJournal of Materials Science, 1990
- Electrical Resistivity of Carbon-Black-Loaded RubbersRubber Chemistry and Technology, 1990
- Threshold tear strength of carbon black filled rubber vulcanizatesJournal of Applied Polymer Science, 1990
- Electrical Conduction in Carbon Black CompositesRubber Chemistry and Technology, 1986
- Dynamic properties of heat‐treated butyl vulcanizatesJournal of Applied Polymer Science, 1963