Lithium insertion into titanium dioxide (anatase) electrodes: microstructure and electrolyte effects

Abstract

Insertion characteristics of anatase electrodes were studied on single-crystal and polycrystalline electrodes of different microstructures. The lithium incorporation from propylene carbonate solution containing LiClO₄ and Li(CF₃SO₂)₂N was studied by means of cyclic voltammetry (CV), the quartz crystal microbalance (QCM) and the galvanostatic intermittent titration technique (GITT). The electrode microstructure affects both the accessible coefficient x and the reversibility of the process. The highest insertion activity was observed for electrodes composed of crystals with characteristic dimensions of ∼10^–8 m. The insertion properties deteriorate for higher as well as for smaller crystal sizes. Enhanced insertion was observed in Li(CF₃SO₂)₂N-containing solutions. Lithium insertion is satisfactorily reversible for mesoscopic electrodes; the reversibility in the case of compact polycrystalline and single-crystal electrodes is poor. The reversibility of the insertion improves with increasing electrolyte concentration. The lithium diffusion coefficient decreases with increasing x and ranges between 10^–15 and 10^–18 cm² s^–1.