The Effect of Titanium Dioxide Alumina Beads on the Photocatalytic Degradation of Picloram in Water
- 27 March 2003
- journal article
- research article
- Published by American Chemical Society (ACS) in Journal of Agricultural and Food Chemistry
- Vol. 51 (9), 2659-2664
- https://doi.org/10.1021/jf026232u
Abstract
Photocatalytic degradation of pesticides with titanium dioxide (TiO(2)) and other catalysts has shown promise as a potential water remediation method. Titanium-based powders have been used in photocatalytic degradation studies but have limitations. The objective of this study was to determine picloram degradation in water using various UV light sources and low-pressure metal organic chemical vapor deposition titanium dioxide alumina beads (TDABs) as a catalyst. A triple-annular, flow-through photoreactor was used as a degradation chamber. A picloram test solution of 50 microg/mL was introduced to the photoreactor inlet and recycled for 10 h at a flow rate of 50 mL/min. Three ultraviolet light sources were compared for their photocatalytic capacity (UV-A, UV-B, and UV-C) both with and without TDABs. TDABs were added to the photoreactor at 1.8 g/cm(3). Dark treatments with and without TDABs were included to quantify hydrolysis or adsorption. A 500-microL aliquot was taken from the test solution 14 times during the 10-h recycling period. Sampling times ranged from 0 to 600 min (10 h). These aliquots were placed in a vial and analyzed by high performance liquid chromatography equipped with a photodiode array detector. Picloram was not significantly hydrolyzed or adsorbed to TDABs during the experiment. The picloram degradation rate with UV-A and TDABs (t(1/2) = 119.5 min) was greater than the degradation rate of UV-A alone (t(1/2)=2288 min). Picloram degradation was not enhanced by the presence of TDABs with either UV-B or UV-C. This may be attributed to inadequate TDAB densities and/or poor light penetration in the photoreactor. Rapid picloram degradation occurred with both UV-B and UV-C, regardless of the presence of TDABs with mean half-lives ranging from 7 to 18 min. These rates were 8 to 16 times faster than picloram degradation using UV-A with TDABs. TDABs' greatest photocatalytic effect was with the lowest energy light source (UV-A). However, picloram degradation was not enhanced when TDABs were combined with more powerful, shorter wavelength light.Keywords
This publication has 13 references indexed in Scilit:
- Photochemical behaviour of dichlorprop [(±)-2-(2,4-dichlorophenoxy)propanoic acid] in aqueous solutionPest Management Science, 2002
- Photocatalytic degradation of propachlor in aqueous TiO2 suspensions. Determination of the reaction pathway and identification of intermediate products by various analytical methodsWater Research, 2002
- Solar photocatalysis: a clean process for water detoxificationScience of The Total Environment, 2001
- Photocatalytic degradation of the herbicides propanil and molinate over aqueous TiO2 suspensions: identification of intermediates and the reaction pathwayApplied Catalysis B: Environment and Energy, 2001
- Photochemical processes for atrazine degradation: methodological approachWater Research, 2001
- Continuous monitoring of photocatalytic treatments by flow injection. Degradation of dicamba in aqueous TiO2 dispersionsChemosphere, 2001
- Photocatalytic oxidation of the herbicide (4-chloro-2-methylphenoxy)acetic acid (MCPA) over TiO2Journal of Photochemistry and Photobiology A: Chemistry, 2001
- Atrazine degradation in a small stream in IowaEnvironmental Science & Technology, 1993
- A comparison of 254 nm and 350 nm excitation of TiO2 in simple photocatalytic reactorsJournal of Photochemistry and Photobiology A: Chemistry, 1992
- Effect of Fluid Flow on Convective Transport in Small CavitiesJournal of the Electrochemical Society, 1990