Tribological properties and structure of ultra-high molecular weight polyethylene after gamma irradiation
- 1 March 2007
- journal article
- research article
- Published by SAGE Publications in Proceedings of the Institution of Mechanical Engineers, Part J: Journal of Engineering Tribology
- Vol. 221 (3), 315-320
- https://doi.org/10.1243/13506501jet227
Abstract
The aim of the present study was to investigate the effects of irradiation and post treatment on the molecular structure, mechanical, and tribological properties of ultra-high molecular weight polyethylene (UHMWPE). UHMWPE was irradiated by gamma ray at doses of 120, 250, and 500 kGy in air and encapsulation by plastic film, and then posttreated in vacuum. The tribological properties were investigated by sliding UHMWPE against Si3N4 ceramic ball on a ball-on-disc tribometer in the presence of distilled water lubricant. The result showed that, after gamma irradiation, the crystallinity and cross-linking degree of UHMWPE increased with dose increasing, whereas its toughness and the elongation decreased sharply. All irradiated samples exhibited lower wear rates with dose in the range from 120 to 250 kGy, but, higher friction coefficients, compared with those un-irradiated. However, over 250 kGy, the wear factor began to increase, which may be associated with the ductile-brittle transition in its mechanical properties. Posttreatment in vacuum promoted residual radicals to cross-link and improved wear resistance of UHMWPE further. The 250 kGy irradiated and posttreated sample showed the best wear resistance. The wear mechanism of un-irradiated UHMWPE and those posttreated ones was mainly plowing, plastic deformation, and adhesion, whereas the irradiated samples were characterized mainly by abrasive wear.Keywords
This publication has 27 references indexed in Scilit:
- Tribological properties of ion implanted UHMWPE against Si3N4 under different lubrication conditionsSurface and Coatings Technology, 2004
- Surface analysis of early retrieved acetabular polyethylene liners: a comparison of conventional and highly crosslinked polyethylenesThe Journal of Arthroplasty, 2004
- Failure micromechanisms during uniaxial tensile fracture of conventional and highly crosslinked ultra-high molecular weight polyethylenes used in total joint replacementsBiomaterials, 2003
- Ion beam modification of surface properties of polyethyleneVacuum, 2003
- Thermomechanical behavior of virgin and highly crosslinked ultra-high molecular weight polyethylene used in total joint replacementsBiomaterials, 2002
- The effect of γ-irradiation on ultra-high molecular weight polyethylene recrystallized under different cooling conditionsRadiation Physics and Chemistry, 2001
- Properties of crosslinked ultra-high-molecular-weight polyethyleneBiomaterials, 2000
- Wear behavior of bulk oriented and fiber reinforced UHMWPEWear, 2000
- The role of polyethylene wear in joint replacement failureProceedings of the Institution of Mechanical Engineers, Part H: Journal of Engineering in Medicine, 1997
- Wear and friction properties of prosthetic joint materials evaluated on a reciprocating pin-on-flat apparatusWear, 1993