Evaluation of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) conduits for peripheral nerve regeneration
- 31 January 2009
- journal article
- Published by Elsevier BV in Biomaterials
- Vol. 30 (2), 217-225
- https://doi.org/10.1016/j.biomaterials.2008.09.036
Abstract
Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) was investigated for possible application in repairing damaged nerves. Porous nerve conduits with both uniform wall porosity and non-uniform wall porosity were prepared using a particle leaching method. Adult Sprague–Dawley (SD) rats weighing 200–250 g were used as the animal model. The conduits were employed to bridge the 10 mm defects in the sciatic nerve of the Sprague–Dawley (SD) rats. Mechanical tests showed that the PHBHHx nerve conduits had proper mechanical properties including maximal loads of 3.1 N and 1.3 N for the conduits with non-uniform wall porosity and with uniform wall porosity, respectively, and maximal stresses of 2.3 MPa and 0.94 MPa for the conduits with non-uniform wall porosity and with uniform wall porosity, respectively. At the same time, both types of conduits were permeable to three compounds tested including glucose, lysozyme and bovine serum albumin, indicating the suitability of the conduits for free exchanges of nutrients. Compound Muscle Action Potentials (CMAPs) were clearly observed in both types of the PHBHHx nerve conduits after 1 month of implantation, indicating a rapid functional recovery for the disrupted nerves. The results of histological sections demonstrated that the internal sides of the conduits with non-uniform wall porosity were compact enough to prevent the connective tissues from ingrowth penetration. After implantation for 3 months in the rats, the conduits with uniform wall porosity and those with non-uniform wall porosity lost 24% and 20% of their original weight average molecular weights, respectively. Combined with the strong mechanical properties, good nerve regeneration ability and non-toxicity of its degradation products, PHBHHx nerve conduits can be developed into a useful material to repair nerve damage.Keywords
This publication has 38 references indexed in Scilit:
- Peripheral nerve regeneration within an asymmetrically porous PLGA/Pluronic F127 nerve guide conduitBiomaterials, 2007
- A Comparison of Polyglycolic Acid Versus Type 1 Collagen Bioabsorbable Nerve Conduits in a Rat Model: An Alternative to AutograftingThe Journal of Hand Surgery, 2007
- The effect of 3-hydroxybutyrate and its derivatives on the growth of glial cellsBiomaterials, 2007
- Radial nerve repair using an autologous denatured muscle graft: comparison with outcomes of nerve graft repairActa Neurochirurgica, 2007
- Physical properties and biocompatibility of a porous chitosan-based fiber-reinforced conduit for nerve regenerationBiotechnology Letters, 2007
- Enhancement of Peripheral Nerve Regeneration Using Bioabsorbable Polymer Tubes Packed With Fibrin GelArtificial Organs, 2007
- Effect of 3-hydroxyhexanoate content in poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) on in vitro growth and differentiation of smooth muscle cellsBiomaterials, 2006
- Peripheral berve regeneration through nerve conduit composed of alginate-collagen-chitosanMacromolecular Research, 2006
- An in vivo study of tricalcium phosphate and glutaraldehyde crosslinking gelatin conduits in peripheral nerve repairJournal of Biomedical Materials Research Part B: Applied Biomaterials, 2005
- Effect of composition of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) on growth of fibroblast and osteoblastBiomaterials, 2005