Effects of porosity on the measured fracture energy of brittle materials
- 1 December 2004
- journal article
- research article
- Published by Taylor & Francis Ltd in Philosophical Magazine
- Vol. 84 (34), 3689-3704
- https://doi.org/10.1080/14786430412331293522
Abstract
Although it is known that growing cracks will interact with pores, it is unclear whether the magnitude of this effect is sufficient to influence the fracture energy. To study this, experiments have been carried out where cracks have been grown through simple distributions of pores in poly(methyl methacrylate). These show that the applied force required to grow the crack between two pores can be greater than that required to grow the crack in the pore-free material. Direct observation during crack growth shows that this increase in applied force is associated with the crack front becoming curved. Based on these observations, the effect of equiaxed pores on the fracture energy of brittle materials has been quantitatively described. The analysis predicts how the relative fracture energy should be influenced by the pore volume fraction, and that it should be independent of the size of the pores or the fracture energy of the matrix. These predictions give good agreement with experimental measurements in different ceramic materials, in which the microstructure of the matrix surrounding the pores does not change with pore volume fraction.Keywords
This publication has 22 references indexed in Scilit:
- Fracture Resistance Measurement Method for in situ Observation of Crack MechanismsJournal of the American Ceramic Society, 1998
- Strain Tolerant Porous Silicon NitrideJournal of the American Ceramic Society, 1997
- Comment on “dependence of ceramics fracture properties on porosity”Journal of Materials Science Letters, 1996
- Fracture behaviour of ceramic laminates in bending—I. Modelling of crack propagationActa Metallurgica et Materialia, 1993
- Dependence of ceramic fracture properties on porosityJournal of Materials Science, 1993
- Porosity dependence of strain of Si3N4 ceramicsJournal of Materials Science Letters, 1988
- Polymorphism and Hydration of Tricalcium Silicate Doped With ZnOJournal of the American Ceramic Society, 1983
- Room-temperature fracture energy of monoclinic Gd2O3Journal of Materials Science, 1981
- Crack shape studies in brittle porous materialsJournal of Materials Science, 1977
- Effects of Porosity on Fracture of Al2O3Journal of the American Ceramic Society, 1973