Preliminary investigation of the NMR, optical and x-ray CT dose–response of polymer gel dosimeters incorporating cosolvents to improve dose sensitivity

Abstract

This study reports on efforts to increase the dose sensitivity of polymer gel dosimeters used in 3D radiation dosimetry. The potential of several different cosolvents is investigated, with the aim of increasing the solubility of N,N'-methylene-bisacrylamide crosslinker in polymer gel dosimeters. Glycerol and isopropanol increase the limit for the crosslinker solubility from approximately 3% to 5% and 10% by weight, respectively. This enables the manufacture of polymer gel dosimeters with much higher levels of crosslinking than was previously possible. New dosimeter recipes containing up to 5 wt% N,N'-methylene-bisacrylamide were subjected to spatially uniform radiation and were studied using nuclear magnetic resonance (NMR), as well as x-ray and optical CT techniques. The resulting dosimeters exhibit dose sensitivities that are up to 2.7 times higher than measured for a typical dosimeters with 3% N,N'-methylene-bisacrylamide without the addition of cosolvent. Two additional cosolvents (n-propanol and sec-butanol) were deemed unsuitable for practical dosimeters due to incompatibility with gelatin, cloudiness prior to irradiation, and immiscibility with water when large quantities of cosolvent were used. The dosimeters with high N,N'-methylene-bisacrylamide content that used isopropanol or glycerol as cosolvents had high optical clarity prior to irradiation, but did not produce suitable optical CT results for non-uniformly irradiated gels due to polymer development outside of the high dose regions of the pencil beams and significant light scatter. Further experiments are required to determine whether cosolvents can be used to manufacture gels with sufficiently high dose sensitivity for readout using x-ray computed tomography.