Segregation and H2 Transport Rate Control in Body-Centered Cubic PdCu Membranes
- 23 August 2007
- journal article
- research article
- Published by American Chemical Society (ACS) in The Journal of Physical Chemistry B
- Vol. 111 (37), 10952-10958
- https://doi.org/10.1021/jp073807n
Abstract
The H2 permeation of a supported 2 microm thick Pd48Cu52 membrane was investigated between 373 and 909 K at DeltaP=0.1 MPa. The initial H2 flux was 0.3 mol.m(-2).s(-1) at 723 K with an ideal H2/N2 selectivity better than 5000. The membrane underwent a bcc-fcc (body-centered cubic to face-centered cubic) phase transition between 723 and 873 K resulting in compositional segregation. After reannealing at 723 K the alloy layer reverted to a bcc structure although a small fcc fraction remained behind. The mixed-phase morphology was analyzed combining X-ray diffraction with scanning electron microscopy-energy-dispersive spectroscopic analysis (SEM-EDS) measurements, which revealed micrometer-scale Cu-enriched bcc and Cu-depleted fcc domains. The H2 flux JH2 of the fcc Pd48Cu52 single phase layer prevailing above 873 K could be described by an Arrhenius law with JH2=(7.6+/-4.9) mol.m(-2).s(-1) exp[(-32.9+/-4.5) kJ.mol(-1)/(RT)]. The characterization of the H2 flux in the mixed-phase region required two Arrhenius laws, i.e., JH2=(1.35+/-0.14) mol.m(-2).s(-1) exp[(-10.3+/-0.5) kJ.mol(-1)/(RT)] between 523 and ca. 700 K and JH2=(56.1+/-9.3) mol.m(-2).s(-1) exp[(-25.3+/-0.6) kJ.mol(-1)/(RT)] below 454 K. The H2 flux exhibited a square root pressure dependence above 523 K, but the pressure exponent gradually increased to 0.77 upon cooling to 373 K. The activation energy and pressure dependence in the intermediate temperature range are consistent with a diffusion-limited H2 transport, while the changes of these characteristics at lower temperatures indicate a desorption-limited H2 flux. The prevalence of desorption as the permeation rate-limiting step below 454 K is attributed to the pairing of an extraordinarily high hydrogen diffusivity with a marginal hydrogen solubility in bcc PdCu alloys. These result in an acceleration of the bulk diffusion rate and a deceleration of the desorption rate, respectively, allowing the bulk diffusion rate to surpass the desorption rate up to relatively high temperatures.Keywords
This publication has 29 references indexed in Scilit:
- Effects of surface activity, defects and mass transfer on hydrogen permeance and n-value in composite palladium-porous stainless steel membranesCatalysis Today, 2006
- High-purity COx-free H2 generation from NH3 via the ultra permeable and highly selective Pd membranesJournal of Membrane Science, 2006
- Electroless plating synthesis, characterization and permeation properties of Pd–Cu membranes supported on ZrO2 modified porous stainless steelJournal of Membrane Science, 2005
- Low-temperature H2 and N2 transport through thin Pd66Cu34Hx layersCatalysis Today, 2005
- Influence of Alloy Composition and Membrane Fabrication on the Pressure Dependence of the Hydrogen Flux of Palladium−Copper MembranesIndustrial & Engineering Chemistry Research, 2003
- Membrane reactors for hydrogenation and dehydrogenation processes based on supported palladiumJournal of Molecular Catalysis A: Chemical, 2001
- Model of hydrogen permeation behavior in palladium membranesJournal of Membrane Science, 1999
- Kinetics of hydrogen desorption from palladium and ruthenium-palladium foilsJournal of Materials Research, 1995
- High temperature thermodynamics of dilute solutions of hydrogen in palladium–copper alloysThe Journal of Chemical Physics, 1979
- Dynamic equilibrium between chemisorbed and absorbed hydrogen in the palladium/hydrogen systemThe Journal of Physical Chemistry, 1973