Thermal Shock Cracking: Design and Assessment Guidelines
- 1 March 2006
- journal article
- Published by ASME International in Journal of Pressure Vessel Technology
- Vol. 129 (1), 125-132
- https://doi.org/10.1115/1.2389029
Abstract
Repeated thermal shock cracking is common in the operation of pressure equipment where water and steam are present. Surprisingly, it is not fully covered in the ASME Boiler and Pressure Vessel code nor in fitness-for-purpose recommended practice such as API 579. An example of thermal shock stresses occurs when hot surfaces are exposed to splashing of cold water. This eventually may lead to crack nucleation and crack growth. However, not all thermal shock cracks lead to failures (such as rupture, leak, or, in more brittle material, fragmentation), indeed the most frequent situation is that the cracking arrests at a depth of a few millimeters. This paper presents a unique experimental study and analysis of the information being gained from this study in terms of design guidelines and crack growth mechanisms. In the experiments, cracks are initiated and then grown in low carbon steel specimens exposed to repeated thermal shock. The test-rigs achieve large thermal shocks through the repeated water quenching of heated flat plate specimens. The effect of steady state loads on the growth and environmental effects due to the aqueous nature of the testing environment are found to be major contributors to the crack growth kinetics. The most important findings are that the conditions leading to both the initiation and the arrest of cracks can be identified and that the depth of a starter notch contributes little to the crack propagation.Keywords
This publication has 8 references indexed in Scilit:
- Potential guidelines for design and fitness for purpose for carbon steel components subject to repeated thermal shockInternational Journal of Pressure Vessels and Piping, 2004
- A two-stage model for predicting crack growth due to repeated thermal shockEngineering Fracture Mechanics, 2003
- Experimental apparatus for thermal shock fatigue investigationsInternational Journal of Pressure Vessels and Piping, 2000
- Remaining life of a vessel containing an internal corner crack under repeated thermal shockProceedings of the Institution of Mechanical Engineers, Part E: Journal of Process Mechanical Engineering, 1997
- Thermal shock fracture experiments on large size plates of A533-B steelInternational Journal of Pressure Vessels and Piping, 1991
- Cleavage and Ductile Thermal Shock Fractures of Corner-Cracked NozzlesJournal of Pressure Vessel Technology, 1989
- Stable and Unstable Crack Growth of A508 Class 3 Plates Subjected to Combined Force of Thermal Shock and TensionJournal of Pressure Vessel Technology, 1989
- A THERMAL SHOCK FATIGUE STUDY OF TYPE 304 AND 316 STAINLESS STEELSFatigue & Fracture of Engineering Materials & Structures, 1981