Atomic layer-deposited tunnel oxide stabilizes silicon photoanodes for water oxidation
- 19 June 2011
- journal article
- Published by Springer Science and Business Media LLC in Nature Materials
- Vol. 10 (7), 539-544
- https://doi.org/10.1038/nmat3047
Abstract
A leading approach for large-scale electrochemical energy production with minimal global-warming gas emission is to use a renewable source of electricity, such as solar energy, to oxidize water, providing the abundant source of electrons needed in fuel synthesis. We report corrosion-resistant, nanocomposite anodes for the oxidation of water required to produce renewable fuels. Silicon, an earth-abundant element and an efficient photovoltaic material, is protected by atomic layer deposition (ALD) of a highly uniform, 2 nm thick layer of titanium dioxide (TiO(2)) and then coated with an optically transmitting layer of a known catalyst (3 nm iridium). Photoelectrochemical water oxidation was observed to occur below the reversible potential whereas dark electrochemical water oxidation was found to have low-to-moderate overpotentials at all pH values, resulting in an inferred photovoltage of ~550 mV. Water oxidation is sustained at these anodes for many hours in harsh pH and oxidative environments whereas comparable silicon anodes without the TiO(2) coating quickly fail. The desirable electrochemical efficiency and corrosion resistance of these anodes is made possible by the low electron-tunnelling resistance (<0.006 Ω cm(2) for p(+)-Si) and uniform thickness of atomic-layer deposited TiO(2).Keywords
This publication has 29 references indexed in Scilit:
- Solar Water Splitting CellsChemical Reviews, 2010
- WO3−Fe2O3 Photoanodes for Water Splitting: A Host Scaffold, Guest Absorber ApproachChemistry of Materials, 2009
- High Density n-Si/n-TiO2Core/Shell Nanowire Arrays with Enhanced PhotoactivityNano Letters, 2009
- Toward Cost-Effective Solar Energy UseScience, 2007
- New Benchmark for Water Photooxidation by Nanostructured α-Fe2O3 FilmsJournal of the American Chemical Society, 2006
- Powering the planet: Chemical challenges in solar energy utilizationProceedings of the National Academy of Sciences of the United States of America, 2006
- Photoelectrochemical Cells of the Electrolyte‐Metal‐Insulator‐Semiconductor (EMIS) Configuration: I . Metal Thickness and Coverage Effects in the Pt/Silicon Oxide/n‐Si SystemJournal of the Electrochemical Society, 1986
- Investigation of a protective conducting silica film on n-siliconElectrochimica Acta, 1984
- Anodic properties of n-Si and n-Ge electrodes in HF solution under illumination and in the darkJournal of Electroanalytical Chemistry and Interfacial Electrochemistry, 1983
- Semiconductor electrodes. 48. Photooxidation of halides and water on n-silicon protected with silicide layersJournal of the American Chemical Society, 1983