Push‐out stress for fibre posts luted using different adhesive strategies
- 14 July 2009
- journal article
- research article
- Published by Wiley in European Journal of Oral Sciences
- Vol. 117 (4), 447-453
- https://doi.org/10.1111/j.1600-0722.2009.00656.x
Abstract
The influence of thermocycling on the bond strength of fibre posts cemented with different luting approaches was investigated. A total of 84 human incisors were selected for the study. Sixty teeth were assigned to one of the following adhesive/cement combinations for push‐out bond‐strength evaluation: group 1, XP Bond/CoreXFlow + DT Light‐Post; group 2, Panavia F 2.0 + Tech 21; or group 3, RelyX Unicem + RelyX. Bonded specimens were cut into 1‐mm‐thick slabs and either thermocycled (40,000 cycles) or stored in artificial saliva (control specimens) before push‐out bond‐strength testing. Additional specimens were processed for quantitative interfacial nanoleakage analysis. Thermocycling decreased the bond strength in specimens of groups 2 and 3, but did not affect the specimens from group 1. No difference was observed among luting approaches in control specimens. Thermocycling resulted in increased silver nitrate deposition (i.e. interfacial nanoleakage) in all groups. Within the limitations of the study, the use of an etch‐and‐rinse adhesive in combination with a dual‐cure cement to lute fiber posts is the most stable luting procedure if compared with a self‐etch resin‐based cement or a self‐adhesive cement, as assayed by thermocycling of the bonded specimens.Keywords
This publication has 22 references indexed in Scilit:
- Static and fatigue fracture resistances of pulpless teeth restored with post–coresDental Materials, 2008
- Effect of post‐space treatment on retention of fiber posts in different root regions using two self‐etching systemsEuropean Journal of Oral Sciences, 2008
- Immediate and 24-Hour Evaluation of the Interfacial Strengths of Fiber PostsJournal of Endodontics, 2006
- Micro-tensile bond strength of adhesives bonded to class-I cavity-bottom dentin after thermo-cyclingDental Materials, 2005
- Geometric Factors Affecting Dentin Bonding in Root Canals: A Theoretical Modeling ApproachJournal of Endodontics, 2005
- In vivo Fluid Movement through Dentin Adhesives in Endodontically Treated TeethJournal of Dental Research, 2005
- Adhesive Dentistry and Endodontics: Materials, Clinical Strategies and Procedures for Restoration of Access Cavities: A ReviewJournal of Endodontics, 2005
- Two Modes of Nanoleakage Expression in Single-step AdhesivesJournal of Dental Research, 2002
- Microtensile bond strength between adhesive cements and root canal dentinDental Materials, 2002
- An in vitro study of the fracture resistance and the incidence of vertical root fracture of pulpless teeth restored with six post-and-core systemsThe Journal of Prosthetic Dentistry, 1999