Measurement of Electrical Steels With Direct Field Determination
- 19 January 2010
- journal article
- Published by Institute of Electrical and Electronics Engineers (IEEE) in IEEE Transactions on Magnetics
- Vol. 46 (2), 298-301
- https://doi.org/10.1109/tmag.2009.2032861
Abstract
The objective of the presented work was to introduce the principles of direct field control into magnetic measurements. Different grades of nonoriented and grain-oriented steels were tested in dc magnetization regime. A vertical array of three Hall sensors was used to control the sample field. With small gradients of the sample surface field our results showed comparable measurement errors with the single sheet tester. Measurement of the hysteresis loss and the coercive force was mostly independent of the field determination method. However, for accurate estimation of the magnetic induction parameters the sample field should be determined directly. No unique dependence was found between the measured dc and 50 Hz Epstein/single sheet tester parameters except the remanent induction of the nonoriented steels.Keywords
This publication has 10 references indexed in Scilit:
- Governing conditions of repeatable Barkhausen noise responseJournal of Magnetism and Magnetic Materials, 2009
- Increase of precision of surface magnetic field measurements by magnetic shieldingMeasurement Science and Technology, 2009
- Applicability of local magnetic measurementsMeasurement, 2008
- Generalization of the Classical Method for Calculating Dynamic Hysteresis Loops in Grain-Oriented Electrical SteelsIEEE Transactions on Magnetics, 2008
- Investigation of applicability of extrapolation method for sample field determination in single-yoke measuring setupJournal of Magnetism and Magnetic Materials, 2006
- Use of novel adaptive digital feedback for magnetic measurements under controlled magnetizing conditionsIEEE Transactions on Magnetics, 2005
- Epstein frame: how and when it can be really representative about the magnetic behavior of laminated magnetic steelsIEEE Transactions on Magnetics, 2005
- Modern State of Nondestructive Testing of Mechanical Properties and Stamping Ability of Steel Sheets in a Manufacturing Technological FlowRussian Journal of Nondestructive Testing, 2003
- 2D analysis of magnetic field strength in GO SiFe steel sheetsJournal de Physique IV, 1998
- Recent advances in the one- and two-dimensional magnetic measurement technique for electrical sheet steelIEEE Transactions on Magnetics, 1990