Control of TiO2 Structures from Robust Hollow Microspheres to Highly Dispersible Nanoparticles in a Tetrabutylammonium Hydroxide Solution
- 14 August 2007
- journal article
- research article
- Published by American Chemical Society (ACS) in Langmuir
- Vol. 23 (19), 9567-9571
- https://doi.org/10.1021/la700797v
Abstract
A new process for controlling the structure of TiO2 from hollow microspheres to highly dispersible nanoparticles has been developed by altering the concentration of tetrabutylammonium hydroxide (TBAH) in the solvothermal reaction of titanium isopropoxide. Robust and size-controllable hollow TiO2 microspheres, constructed by the assembly of 18 nm TiO2 nanoparticles, were synthesized at relatively high TBAH concentration. The diameters of hollow spheres, with a shell thickness of approximately 250 nm, were controlled to 1.5-4 microm by varying the concentration of TBAH in the range of 0.1-0.5 M. After calcination at 450 degrees C, the hollow microspheres were not appreciably deformed and were still floating on the surface of the water. However, highly dispersible TiO2 nanoparticles with an average diameter of 13 nm were obtained at a low TBAH concentration such as 9.2 mM. The colloidal particle size of TiO2 in an aqueous suspension at pH 2 was 12.5-13.5 nm, which indicates that the each nanoparticle is completely separated. The overall procedure is simple and highly reproducible, and large-scale synthesis is available at low cost.Keywords
This publication has 45 references indexed in Scilit:
- Modeling of nanostructured TiO2 spheres obtained by ultrasonic spray pyrolysisColloids and Surfaces A: Physicochemical and Engineering Aspects, 2004
- Designing of nanostructured hollow TiO2 spheres obtained by ultrasonic spray pyrolysisJournal of Colloid and Interface Science, 2004
- Photoelectrochemical cellsNature, 2001
- Ultrafast colour displaysNature, 2001
- Concluding remarks on heterogeneous solar photocatalysisSolar Energy Materials and Solar Cells, 1995
- Environmental Applications of Semiconductor PhotocatalysisChemical Reviews, 1995
- A low-cost, high-efficiency solar cell based on dye-sensitized colloidal TiO2 filmsNature, 1991
- Photocatalytic degradation of organic water contaminants: Mechanisms involving hydroxyl radical attackJournal of Catalysis, 1990
- Photoelectrochemistry: Applications to Solar Energy ConversionAnnual Review of Physical Chemistry, 1978
- Biological Sciences: One and Two-dimensional Structure of Alpha-Helix and Beta-Sheet Forms of Poly(L-Alanine) shown by Specific Heat Measurements at Low Temperatures (1.5–20 K)Nature, 1972