Fabrication of three-dimensional porous cell-laden hydrogel for tissue engineering
- 1 September 2010
- journal article
- Published by IOP Publishing in Biofabrication
- Vol. 2 (3), 035003
- https://doi.org/10.1088/1758-5082/2/3/035003
Abstract
For tissue engineering applications, scaffolds should be porous to enable rapid nutrient and oxygen transfer while providing a three-dimensional (3D) microenvironment for the encapsulated cells. This dual characteristic can be achieved by fabrication of porous hydrogels that contain encapsulated cells. In this work, we developed a simple method that allows cell encapsulation and pore generation inside alginate hydrogels simultaneously. Gelatin beads of 150-300 microm diameter were used as a sacrificial porogen for generating pores within cell-laden hydrogels. Gelation of gelatin at low temperature (4 degrees C) was used to form beads without chemical crosslinking and their subsequent dissolution after cell encapsulation led to generation of pores within cell-laden hydrogels. The pore size and porosity of the scaffolds were controlled by the gelatin bead size and their volume ratio, respectively. Fabricated hydrogels were characterized for their internal microarchitecture, mechanical properties and permeability. Hydrogels exhibited a high degree of porosity with increasing gelatin bead content in contrast to nonporous alginate hydrogel. Furthermore, permeability increased by two to three orders while compressive modulus decreased with increasing porosity of the scaffolds. Application of these scaffolds for tissue engineering was tested by encapsulation of hepatocarcinoma cell line (HepG2). All the scaffolds showed similar cell viability; however, cell proliferation was enhanced under porous conditions. Furthermore, porous alginate hydrogels resulted in formation of larger spheroids and higher albumin secretion compared to nonporous conditions. These data suggest that porous alginate hydrogels may have provided a better environment for cell proliferation and albumin production. This may be due to the enhanced mass transfer of nutrients, oxygen and waste removal, which is potentially beneficial for tissue engineering and regenerative medicine applications.Keywords
This publication has 42 references indexed in Scilit:
- Hydrogels in Regenerative MedicineAdvanced Materials, 2009
- Designing Temperature-Responsive Biocompatible Copolymers and Hydrogels Based on 2-Hydroxyethyl(meth)acrylatesBiomacromolecules, 2008
- In vitro and in vivo test of PEG/PCL-based hydrogel scaffold for cell delivery applicationJournal of Controlled Release, 2007
- Microscale culture of human liver cells for drug developmentNature Biotechnology, 2007
- Porous Thermoresponsive-co-Biodegradable Hydrogels as Tissue-Engineering Scaffolds for 3-Dimensional In Vitro Culture of ChondrocytesTissue Engineering, 2007
- Microfluidic scaffolds for tissue engineeringNature Materials, 2007
- Photo-patterning of porous hydrogels for tissue engineeringBiomaterials, 2007
- Fabrication of 3D hepatic tissues by additive photopatterning of cellular hydrogelsThe FASEB Journal, 2006
- Porous scaffold design for tissue engineeringNature Materials, 2005
- Culture of primary rat hepatocytes within porous chitosan scaffoldsJournal of Biomedical Materials Research Part A, 2003