Correlation between passive film-induced stress and stress corrosion cracking of α-Ti in a methanol solution at various potentials
- 15 April 2003
- journal article
- Published by Elsevier BV in Materials Science and Engineering: A
- Vol. 346 (1-2), 1-7
- https://doi.org/10.1016/s0921-5093(02)00529-4
Abstract
No abstract availableKeywords
This publication has 10 references indexed in Scilit:
- Stress corrosion cracking relation with dezincification layer-induced stressMetallurgical and Materials Transactions, 2001
- Stress Corrosion Cracking Caused by Passive Film-Induced Tensile StressCorrosion, 2000
- In-Situ Transmission Electron Microscopic Observation of Corrosion-Enhanced Dislocation Emission and Crack Initiation of Stress CorrosionCorrosion, 2000
- NUCLEATION, BLUNTING OR PROPAGATION OF A NANOCRACK IN DISLOCATION‐FREE ZONES OF THIN CRYSTALSFatigue & Fracture of Engineering Materials & Structures, 1998
- Determination of tensile stress induced by dezincification layer during corrosion for brassCorrosion Science, 1998
- In-situ TEM observation of dissolution-enhanced dislocation emission, motion and the nucleation of SCC for Ti24Al11Nb alloy in methanolScripta Materialia, 1997
- In situtem observations of nucleation and bluntness of nanocracks in thin crystals of 310 stainless steelActa Metallurgica et Materialia, 1995
- The in-situ TEM observation of corrosion facilitating dislocation emission, multiplication and motion for brassScripta Metallurgica et Materialia, 1995
- The effect of anodic polarization on the ambient creep of brassCorrosion Science, 1994
- Stress generation during anodic oxidation of titanium and aluminumCorrosion Science, 1993