Oil Core−Polymer Shell Microcapsules Prepared by Internal Phase Separation from Emulsion Droplets. I. Characterization and Release Rates for Microcapsules with Polystyrene Shells
- 19 November 2004
- journal article
- Published by American Chemical Society (ACS) in Langmuir
- Vol. 20 (26), 11374-11379
- https://doi.org/10.1021/la048561h
Abstract
Microcapsules with an oil core surrounded by a polymeric shell have been prepared by the controlled phase separation of polymer dissolved within the oil droplets of an oil-in-water emulsion. The dispersed oil phase consists of the shell polymer (polystyrene), a good solvent for the polymer (dichloromethane), and a poor solvent for the polymer (typically hexadecane). Removal of the good solvent results in phase separation of the polymer within the oil droplets. If the three interfacial tensions between the core oil, the shell-forming polymer, and the continuous phase are of the required relative magnitudes, a polymer shell forms surrounding the poor solvent. A UV-responsive organic molecule was added to the oil phase, prior to emulsification, to investigate the release of a model active ingredient from the microcapsules. This molecule should be soluble in the organic core but also have some water solubility to provide a driving force for release into the continuous aqueous phase. As the release rate of the active ingredient is a function of the thickness of the polymeric shell, for controlled release applications, it is necessary to control this parameter. For the preparative method described here, the thickness of the shell formed is directly related to the mass of polymer dissolved in the oil phase. The rate of volatile solvent removal influences the porosity of the polymer shell. Rapid evaporation leads to cracks in the shell and a relatively fast release rate of the active ingredient. If a more gentle evaporation method is employed, the porosity of the polymer shell is decreased, resulting in a reduction in release rate. Cross-linking the polymer shell after capsule formation was also found to decrease both the release rate and the yield of the active ingredient. The nature of the oil core also affected the release yield.Keywords
This publication has 25 references indexed in Scilit:
- Release Behavior of Thin-Walled Microcapsules Composed of Polyelectrolyte MultilayersLangmuir, 2001
- Preparation and characterization of polyethyl-2-cyanoacrylate nanocapsules containing antiepileptic drugsBiomaterials, 1996
- Physico-chemical evaluation of acetylsalicylic acid-Eudragit® RS100 microspheres prepared using a solvent-partition methodJournal of Microencapsulation, 1995
- Polyanhydride microspheres. IV. Morphology and characterization of systems made by spray dryingJournal of Applied Polymer Science, 1992
- Preparation of biodegradable microspheres and microcapsules: 2. Polyactides and related polyestersJournal of Controlled Release, 1991
- Factors influencing the profiles of TRH release from copoly(d,l-lactic/glycolic acid) microspheresInternational Journal of Pharmaceutics, 1991
- Effects of counteranion of TRH and loading amount on control of TRH release from copoly(dl-lactic/glycolic acid) microspheres prepared by an in-water drying methodInternational Journal of Pharmaceutics, 1991
- Preparation of Biodegradable Poly(±)lactide Microparticles Using a Spray-Drying TechniqueJournal of Pharmacy and Pharmacology, 1988
- A method for the preparation of polylactic acid microcapsules of controlled particle size and drug loadingJournal of Microencapsulation, 1988
- Solubility Studies. IV. The Solubilities of Certain Slightly Soluble Organic Compounds in Water1Journal of the American Chemical Society, 1933