Study of Biodegradable Polylactide/Poly(butylene adipate-co-terephthalate) Blends
Top Cited Papers
- 23 November 2005
- journal article
- research article
- Published by American Chemical Society (ACS) in Biomacromolecules
- Vol. 7 (1), 199-207
- https://doi.org/10.1021/bm050581q
Abstract
Both polylactide (PLA) and poly(butylene adipate-co-terephthalate) (PBAT) are biodegradable polymers. They are thermoplastics which can be processed using most conventional polymer processing methods. PLA is high in strength and modulus (63 MPa and 3.4 GPa, respectively) but brittle (strain at break 3.8%) while PBAT is flexible and tough (strain at break ∼710%). In view of their complementary properties, blending PLA with PBAT becomes a natural choice to improve PLA properties without compromising its biodegradability. In this study, PLA and PBAT were melt blended using a twin screw extruder. Melt elasticity and viscosity of the blends increased with the concentration of PBAT. Crystallization of the PLA component, phase morphology of the blend, mechanical properties, and toughening mechanism were investigated. The blend comprised an immiscible, two-phase system with the PBAT evenly dispersed in the form of ∼300 nm domains within the PLA matrix. The PBAT component accelerated the crystallization rate of PLA but had little effect on its final degree of crystallinity. With the increase in PBAT content (5−20 wt %), the blend showed decreased tensile strength and modulus; however, elongation and toughness were dramatically increased. With the addition of PBAT, the failure mode changed from brittle fracture of the neat PLA to ductile fracture of the blend as demonstrated by tensile test and scanning electron microcopy (SEM) micrographs. Debonding between the PLA and PBAT domains induced large plastic deformation in PLA matrix ligaments.Keywords
This publication has 25 references indexed in Scilit:
- Immiscible Poly(L‐lactide)/Poly(ε‐caprolactone) Blends: Influence of the Addition of a Poly(L‐lactide)‐Poly(oxyethylene) Block Copolymer on Thermal Behavior and MorphologyMacromolecular Chemistry and Physics, 2004
- Properties of lactic acid based polymers and their correlation with compositionProgress in Polymer Science, 2002
- Use of Iron Monocarboxylates in the Two-Step Preparation of Poly(ester−urethane)sBiomacromolecules, 2001
- LCST phase separation in biodegradable polymer blends: poly(D,L-lactide) and poly(ε-caprolactone)Macromolecular Chemistry and Physics, 2000
- Interfacial Properties of Mixed Polyethylene Glycol/Poly(d,l-lactide-co-glycolide) Films Spread at the Air/Water InterfaceLangmuir, 1999
- Miscibility and crystallization behaviour of poly(l-lactide)/poly(p-vinylphenol) blendsPolymer, 1998
- Impact modification of lactic acid based poly(ester-urethanes) by blendingJournal of Applied Polymer Science, 1997
- Synthesis and degradability of a novel aliphatic polyester: poly(β-methyl-δ-valerolactone-co-L-lactide)Polymer, 1995
- Influence of particle size and particle size distribution on toughening mechanisms in rubber-modified epoxiesJournal of Materials Science, 1991
- Electron microscopy of crazes in polystyrene and rubber modified polystyrene: use of iodine-sulphur eutectic as a craze reinforcing impregnantPolymer, 1971