Activated carbon with ultrahigh specific surface area synthesized from natural plant material for lithium–sulfur batteries
- 30 July 2014
- journal article
- research article
- Published by Royal Society of Chemistry (RSC) in Journal of Materials Chemistry A
- Vol. 2 (38), 15889-15896
- https://doi.org/10.1039/c4ta03503h
Abstract
Porous activated carbon with a ultrahigh specific surface area (3164 m2 g−1) and large pore volume (1.88 cm3 g−1) was prepared from waste litchi shells with channel-like macropores via a KOH activation method. The macroporous structure of litchi shells is believed to be conducive to distribute the activation agent, which enables sufficient activation. The as-prepared activated carbon was developed as a conducting framework for lithium–sulfur battery cathode materials. The resulting activated carbon/sulfur composite cathode possesses a high specific capacity, good rate capability, and long-term cycling performance. At 200 mA g−1 current density, the initial discharge capacity of the activated carbon/sulfur composite cathode with 60 wt% sulfur content is 1105 mA h g−1. At a current density of 800 mA g−1, the activated carbon/sulfur composite cathode shows 51% capacity retention over 800 cycles with a fade rate of 0.06% per cycle. The coulombic efficiency of the cell remains at approximately 95%. By adding LiNO3 in the electrolyte, the activated carbon/sulfur composite electrode tested at 800 mA g−1 shows a high coulombic efficiency (>99%). The activated carbon/sulfur composites exhibited similar capacity value and cycling trends with an increase in sulfur content from 60% to 68%. The good electrochemical performance can be attributed to the excellent structural parameters of the activated carbon. The ultrahigh specific surface area and large pore volume not only enhances the sulfur content but also ensures dispersion of elemental sulfur in the conducting framework, thereby improving sulfur utilization. The small nanopores of the activated carbon can effectively inhibit the diffusion of polysulfides during the charge/discharge process.Keywords
This publication has 48 references indexed in Scilit:
- Lithium–Sulfur Batteries: Electrochemistry, Materials, and ProspectsAngewandte Chemie-International Edition, 2013
- Porous carbon nanotubes improved sulfur composite cathode for lithium-sulfur batteryJournal of Solid State Electrochemistry, 2013
- Nanostructured sulfur cathodesChemical Society Reviews, 2013
- Composite of sulfur impregnated in porous hollow carbon spheres as the cathode of Li-S batteries with high performanceNano Research, 2012
- Chemically tailoring the nanostructure of graphenenanosheets to confine sulfur for high-performance lithium-sulfur batteriesJournal of Materials Chemistry A, 2012
- Confining Sulfur in Double‐Shelled Hollow Carbon Spheres for Lithium–Sulfur BatteriesAngewandte Chemie, 2012
- Lithium/Sulfur Cell Discharge Mechanism: An Original Approach for Intermediate Species IdentificationAnalytical Chemistry, 2012
- Li–O2 and Li–S batteries with high energy storageNature Materials, 2011
- Advances in Li–S batteriesJournal of Materials Chemistry, 2010
- A highly ordered nanostructured carbon–sulphur cathode for lithium–sulphur batteriesNature Materials, 2009