Polylactide Stereocomplexation Leads to Higher Hydrolytic Stability but More Acidic Hydrolysis Product Pattern
- 4 March 2010
- journal article
- Published by American Chemical Society (ACS) in Biomacromolecules
- Vol. 11 (4), 1067-1073
- https://doi.org/10.1021/bm100029t
Abstract
Poly-l-lactide/poly-d-lactide (PLLA/PDLA) stereocomplex had much higher hydrolytic stability compared to plain PLLA, but at the same time shorter and more acidic degradation products were formed. Both materials were subjected to hydrolytic degradation in water and in phosphate buffer at 37 and 60 °C, and the degradation processes were monitored by following mass loss, water uptake, thermal properties, surface changes, and pH of the aging medium. The degradation product patterns were determined by electrospray ionization-mass spectrometry (ESI-MS). The high crystallinity and strong secondary interactions in the stereocomplex prevented water uptake and resulted in lower mass loss and degradation rate. However, somewhat surprisingly, the pH of the aging medium decreased much faster in the case of PLLA/PDLA stereocomplex. In accordance, the ESI-MS results showed that hydrolysis of PLLA/PDLA resulted in shorter and more acidic degradation products. This could be explained by the increased intermolecular crystallization due to stereocomplexation, which results in an increased number of tie chains. Because mainly these short tie chains are susceptible to hydrolysis this leads to formation of shorter oligomers compared to hydrolysis of regular PLLA.Keywords
This publication has 29 references indexed in Scilit:
- Hydrolytic Degradation Behavior of a Renewable Thermoplastic ElastomerBiomacromolecules, 2009
- Degradation Products of Aliphatic and Aliphatic–Aromatic PolyestersPublished by Springer Science and Business Media LLC ,2008
- Branched Poly(lactide) Synthesized by Enzymatic Polymerization: Effects of Molecular Branches and Stereochemistry on Enzymatic Degradation and Alkaline HydrolysisBiomacromolecules, 2007
- Kinetics and Time−Temperature Equivalence of Polymer DegradationBiomacromolecules, 2007
- Properties of lactic acid based polymers and their correlation with compositionProgress in Polymer Science, 2002
- In vitro hydrolysis of blends from enantiomeric poly(lactide)s Part 1. Well-stereo-complexed blend and non-blended filmsPolymer, 2000
- Properties and morphology of poly(L-lactide). II. hydrolysis in alkaline solutionJournal of Polymer Science Part A: Polymer Chemistry, 1998
- Weight losses and molecular weight changes correlated with the evolution of hydroxyacids in simulated in vivo degradation of homo- and copolymers of PLA and PGAPolymer Degradation and Stability, 1996
- Degradation of high molecular weight poly(l-lactide) in alkaline mediumBiomaterials, 1995
- Hydrolytic degradation of devices based on poly(dl-lactic acid) size-dependenceBiomaterials, 1995