Characterization of the interaction layer grown by interdiffusion between U–7wt%Mo and Al A356 alloy at 550 and 340°C
- 28 February 2009
- journal article
- research article
- Published by Elsevier BV in Journal of Nuclear Materials
- Vol. 384 (3), 268-273
- https://doi.org/10.1016/j.jnucmat.2008.11.035
Abstract
No abstract availableThis publication has 10 references indexed in Scilit:
- Effect of Si and Zr on the interdiffusion of U–Mo alloy and AlJournal of Nuclear Materials, 2008
- Evidence for the presence of U–Mo–Al ternary compounds in the U–Mo/Al interaction layer grown by thermal annealing: a coupled micro X-ray diffraction and micro X-ray absorption spectroscopy studyJournal of Applied Crystallography, 2007
- Growth Kinetics of Intermetallic Phases in U-Mo vs. Al Alloy Diffusion Couples Annealed at 550°CDefect and Diffusion Forum, 2007
- Post-irradiation examination of uranium–7wt% molybdenum atomized dispersion fuelJournal of Nuclear Materials, 2004
- Microstructure of U3Si2 fuel plates submitted to a high heat fluxJournal of Nuclear Materials, 2004
- Characterization of the reaction layer in U–7wt%Mo/Al diffusion couplesJournal of Nuclear Materials, 2003
- Reaction layer growth and reaction heat of U–Mo/Al dispersion fuels using centrifugally atomized powdersJournal of Nuclear Materials, 2003
- Low-temperature irradiation behavior of uranium–molybdenum alloy dispersion fuelJournal of Nuclear Materials, 2002
- Phase formation and growth at interface between U3Si and aluminiumJournal of Nuclear Materials, 1991
- Etude des alliages aluminium-uranium application a la transformation a l'etat solide UAl3 → UAl4Journal of Nuclear Materials, 1959