Bipolar Cu/HfO2/p++ Si Memristors by Sol-Gel Spin Coating Method and Their Application to Environmental Sensing
Open Access
- 10 July 2019
- journal article
- research article
- Published by Springer Science and Business Media LLC in Scientific Reports
- Vol. 9 (1), 1-15
- https://doi.org/10.1038/s41598-019-46443-x
Abstract
In this paper, the memristive switching behavior of Cu/ HfO2/p++ Si devices fabricated by an organic-polymer-assisted sol-gel spin-coating method, coupled with post-annealing and shadow-mask metal sputtering steps, is examined. HfO2 layers of about 190 nm and 80 nm, are established using cost-effective spin-coating method, at deposition speeds of 2000 and 4000 rotations per minute (RPM), respectively. For two types of devices, the memristive characteristics (Von, Ion, and Vreset) and device-to-device electrical repeatability are primarily discussed in correlation with the oxide layer uniformity and thickness. The devices presented in this work exhibit an electroforming free and bipolar memory-resistive switching behavior that is typical of an Electrochemical Metallization (ECM) I-V fingerprint. The sample devices deposited at 4000 RPM generally show less variation in electrical performance parameters compared to those prepared at halved spin-coating speed. Typically, the samples prepared at 4000 RPM (n = 8) display a mean switching voltage Von of 3.0 V (±0.3) and mean reset voltage Vreset of −1.1 V (±0.5) over 50 consecutive sweep cycles. These devices exhibit a large Roff/Ron window (up to 104), and sufficient electrical endurance and retention properties to be further examined for radiation sensing. As they exhibit less statistical uncertainty compared to the samples fabricated at 2000 RPM, the devices prepared at 4000 RPM are tested for the detection of soft gamma rays (emitted from low-activity Cs-137 and Am-241 radioactive sources), by assessing the variation in the on-state resistance value upon exposure. The analysis of the probability distributions of the logarithmic Ron values measured over repeated ON-OFF cycles, before, during and after exposing the devices to radiation, demonstrate a statistical difference. These results pave the way for the fabrication and development of cost-effective soft-gamma ray detectors.Keywords
Funding Information
- UAE Space Agency, Abu Dhabi, UAE
This publication has 80 references indexed in Scilit:
- Real‐Time Observation on Dynamic Growth/Dissolution of Conductive Filaments in Oxide‐Electrolyte‐Based ReRAMAdvanced Materials, 2012
- In Situ Observation of Voltage‐Induced Multilevel Resistive Switching in Solid Electrolyte MemoryAdvanced Materials, 2011
- Metal nanocrystal memory with sol–gel derived HfO2 high-κ tunnel oxideThin Solid Films, 2011
- Electrochemical metallization memories—fundamentals, applications, prospectsNanotechnology, 2011
- Electrode dependence of filament formation in HfO2 resistive-switching memoryJournal of Applied Physics, 2011
- Resistance switching in HfO2 metal-insulator-metal devicesJournal of Applied Physics, 2010
- Low-Power Switching of Nonvolatile Resistive Memory Using Hafnium OxideJapanese Journal of Applied Physics, 2007
- Evaluation of a low-cost commercial mosfet as radiation dosimeterSensors and Actuators A: Physical, 2006
- Sources, Effects and Risks of Ionizing RadiationRadiation Research, 1989
- Switching properties of thin Nio filmsSolid-State Electronics, 1964