Evolution of precipitates, in particular cruciform and cuboid particles, during simulated direct charging of thin slab cast vanadium microalloyed steels
- 1 June 2004
- journal article
- Published by SAGE Publications in Materials Science and Technology
- Vol. 20 (6), 720-730
- https://doi.org/10.1179/026708304225016743
Abstract
A study has been undertaken of four vanadium based steels which have been processed by a simulated direct charging route using processing parameters typical of thin slab casting, where the cast product has a thickness of 50 to 80mm ( in this study 50 mm) and is fed directly to a furnace to equalise the microstructure prior to rolling. In the direct charging process, cooling rates are faster, equalisation times shorter and the amount of deformation introduced during rolling less than in conventional practice. Samples in this study were quenched after casting, after equalisation, after 4th rolling pass and after coiling, to follow the evolution of microstructure. The mechanical and toughness properties and the microstructural features might be expected to differ from equivalent steels, which have undergone conventional processing. The four low carbon steels (~0.06wt%) which were studied contained 0.1wt%V (V-N), 0.1wt%V and 0.010wt%Ti (V-Ti), 0.1wt%V and 0.03wt%Nb (V-Nb), and 0.1wt%V, 0.03wt%Nb and 0.007wt%Ti (V-Nb-Ti). Steels V-N and V-Ti contained around 0.02wt% N, while the other two contained about 0.01wt%N. The as-cast steels were heated at three equalising temperatures of 1050C, 1100C or 1200C and held for 30-60 minutes prior to rolling. Optical microscopy and analytical electron microscopy, including parallel electron energy loss spectroscopy (PEELS), were used to characterise the precipitates. In the as-cast condition, dendrites and plates were found. Cuboid particles were seen at this stage in Steel V-Ti, but they appeared only in the other steels after equalization. In addition, in the final product of all the steels, fine particles were seen, but it was only in the two titanium steels that cruciform precipitates were present. PEELS analysis showed that the dendrites, plates, cuboids, cruciforms and fine precipitates were essentially nitrides. The two Ti steels had better toughness than the other steels but inferior lower yield stress values. This was thought to be, in part, due to the formation of cruciform precipitates in austenite, thereby removing nitrogen and the microalloying elements which would have been expected to precipitate in ferrite as dispersion hardening particlesKeywords
This publication has 15 references indexed in Scilit:
- Improving the analysis of small precipitates in HSLA steels using a plasma cleaner and ELNESUltramicroscopy, 2002
- The Evolution of Microstructure during Thin Slab Direct Rolling Processing in Vanadium Microalloyed Steels.ISIJ International, 2002
- The effects of thermomechanical processing on the precipitation in an industrial dual-phase steel microalloyed with titaniumMetallurgical and Materials Transactions A, 2001
- Precipitation behavior in a medium carbon, ti-v-n microalloyed steelMetallurgical and Materials Transactions A, 1996
- The Evolution of Precipitates in Nb-Ti Microalloyed Steels during Solidification and Post-solidification Cooling.ISIJ International, 1996
- Solidification Microstructure of Strip Cast Ti-SteelCanadian Metallurgical Quarterly, 1994
- Recrystallization controlled rolling and accelerated cooling for high strength and toughness in V-Ti-N steelsMetallurgical Transactions A, 1991
- Analysis of small vanadium carbide precipitates using Electron Energy Loss SpectroscopyUltramicroscopy, 1989
- Nature of large precipitates in titanium-containing HSLA steelsMaterials Science and Technology, 1987
- Einfluß der Abbindung von Stickstoff durch Aluminium und Vanadin auf die mechanischen Eigenschaften von hochfesten BaustählenArchiv für das Eisenhüttenwesen, 1964