Effects of phosphate-buffered saline concentration and incubation time on the mechanical and structural properties of electrochemically aligned collagen threads
- 4 May 2011
- journal article
- Published by IOP Publishing in Biomedical Materials
- Vol. 6 (3), 035008
- https://doi.org/10.1088/1748-6041/6/3/035008
Abstract
A key step during the synthesis of collagen constructs is the incubation of monomeric collagen in phosphate buffer saline (PBS) to promote fibrillogenesis in the collagen network. Optimal PBS-treatment conditions for monomeric collagen solutions to induce gelation are well established in the literature. Recently, a report in the literature (Cheng et al 2008 Biomaterials 29 3278-88) showed a novel method to fabricate highly oriented electrochemically aligned collagen (ELAC) threads which have orders of magnitude greater packing density than collagen gels. The optimal PBS-treatment conditions for induction of D-banding pattern in such a dense and anisotropic collagen network are unknown. This study aimed to optimize PBS treatment of ELAC threads by investigating the effect of phosphate ion concentration (0.5×, 1×, 5× and 10×) and incubation time (3, 12 and 96 h) on the mechanical strength and ultrastructural organization by monotonic mechanical testing, small angle x-ray scattering and transmission electron microscopy (TEM). ELAC threads incubated in water (no PBS) served as the control. ELAC threads incubated in 1× PBS showed significantly higher extensibility compared to those in 0.5× or 10× PBS along with the presence of D-banded patterns with a periodicity of 63.83 nm. Incubation of ELAC threads in 1× PBS for 96 h resulted in significantly higher ultimate stress compared to 3 or 12 h. However, these threads lacked the D-banding pattern. TEM observations showed no significant differences in the microfibril diameter distribution of ELAC threads treated with or without PBS. This indicates that microfibrils lacked D-banding following electrochemical alignment and the subsequent PBS-treatment-induced D-banding by reorganization within microfibrils. It was concluded that incubation of aligned collagen in 1× PBS for 12 h results in mechanically competent, D-banded ELAC threads which can be used for the regeneration of load bearing tissues such as tendons and ligaments.Keywords
This publication has 44 references indexed in Scilit:
- Dense type I collagen matrices that support cellular remodeling and microfabrication for studies of tumor angiogenesis and vasculogenesis in vitroBiomaterials, 2010
- Comparison of morphology, orientation, and migration of tendon derived fibroblasts and bone marrow stromal cells on electrochemically aligned collagen constructsJournal of Biomedical Materials Research Part A, 2010
- Fibrillogenesis in continuously spun synthetic collagen fiberJournal of Biomedical Materials Research Part B: Applied Biomaterials, 2009
- Fibrillogenesis in Dense Collagen Solutions: A Physicochemical StudyJournal of Molecular Biology, 2008
- Decreasing Inflammatory Response of Injured Patellar Tendons Results in Increased Collagen Fibril DiametersConnective Tissue Research, 2005
- Interactions of Inorganic Phosphate and Sulfate Anions with CollagenBiochemistry, 2004
- Assembly of collagen into microribbons: effects of pH and electrolytesJournal of Structural Biology, 2004
- Identification of collagen fibril fusion during vertebrate tendon morphogenesis. The process relies on unipolar fibrils and is regulated by collagen-proteoglycan interactionJournal of Molecular Biology, 2000
- Self-assembly of collagen fibers. Influence of fibrillar alignment and decorin on mechanical propertiesBiophysical Journal, 1997
- Native collagen fibrils from echinoderms are molecularly bipolarJournal of Molecular Biology, 1994