Study of hydrogen concentration dependent growth of external annular crack in round tensile specimen using cohesive zone model
- 31 July 2013
- journal article
- Published by Elsevier BV in Engineering Fracture Mechanics
- Vol. 106, 49-66
- https://doi.org/10.1016/j.engfracmech.2013.04.007
Abstract
No abstract availableKeywords
This publication has 30 references indexed in Scilit:
- Modelling of mode-I stable crack growth under hydrogen assisted stress corrosion crackingEngineering Fracture Mechanics, 2011
- Testing and mesoscale modelling of hydrogen assisted cracking of magnesiumEngineering Fracture Mechanics, 2010
- Effects of hydrogen on steady, ductile crack growth: Computational studiesInternational Journal of Solids and Structures, 2009
- Modelling of hydrogen diffusion and hydrogen induced cracking in supermartensitic and duplex stainless steelsMaterials & Design (1980-2015), 2008
- Simulation of hydrogen assisted stress corrosion cracking using the cohesive modelEngineering Fracture Mechanics, 2008
- A Prediction Model for Hydrogen Induced Cracking in a Prestressed Wire with a Fracture AnalysisISIJ International, 2008
- Determination of the critical hydrogen concentration for delayed fracture of high strength steel by constant load test and numerical calculationCorrosion Science, 2006
- Effect of residual stress-strain profiles on hydrogen-induced fracture of prestressing steel wiresMaterials Science, 2006
- Computer simulation of intergranular stress corrosion cracking via hydrogen embrittlementModelling and Simulation in Materials Science and Engineering, 2000
- Crack growth from internal hydrogen—temperature and microstructural effects in 4340 steelMetallurgical Transactions A, 1988