Brittle fracture of gas turbine blade caused by the formation of primary β-NiAl phase in Ni-base superalloy
- 1 December 2012
- journal article
- Published by Elsevier BV in Engineering Failure Analysis
- Vol. 26, 318-324
- https://doi.org/10.1016/j.engfailanal.2012.07.014
Abstract
No abstract availableThis publication has 15 references indexed in Scilit:
- Primary α phase and its effect on the impact ductility of a high Cr content cast Ni-base superalloyJournal of Alloys and Compounds, 2012
- Influences of annealing and hafnium concentration on the microstructures of sputter deposited β-NiAl coatings on superalloy substratesIntermetallics, 2010
- Failure analysis of two sets of aircraft bladesEngineering Failure Analysis, 2010
- Study of the fracture of the last stage blade in an aircraft gas turbineEngineering Failure Analysis, 2009
- Formation and characterisation of NiAl‐Ti coating on nickel‐based superalloy B1900Surface and Interface Analysis, 2009
- Formation of secondary reaction zone in ruthenium bearing nickel based single crystal superalloys with diffusion aluminide coatingsMaterials Science and Technology, 2009
- A novel route to BaMgAl10O17:Eu blue phosphor by nano-coating methodMaterials Science and Engineering B, 2008
- Microstructural aspects of the failure analysis of nickel base superalloys componentsEngineering Failure Analysis, 2005
- Common failures in gas turbine bladesEngineering Failure Analysis, 2005
- Influencing Factors of Stress Rupture at 750 °C Temperature for Cast Nickel Base Superalloy K403Key Engineering Materials, 1999