Degradation of Norway spruce (Picea abies) heartwood and sapwood during 5.5 years’ above-ground exposure
- 1 September 2008
- journal article
- research article
- Published by Taylor & Francis Ltd in Wood Material Science & Engineering
- Vol. 3 (3-4), 83-93
- https://doi.org/10.1080/17480270902774886
Abstract
Differences in durability between heartwood and sapwood of Norway spruce [Picea abies (L.) Karst.] were investigated to determine wood qualities most favourable for use in outdoor constructions above ground. Trees grown on sites with either good or poor access to water were used. Seventy-eight specimens measuring 20 × 50 × 300 mm3 separated into heartwood and sapwood, half untreated, half painted, were exposed horizontally outdoors above ground for 5.5 years with the pith side up and the bark side down. Crack length and crack number were measured. Fungus growth and surface changes were visually estimated. Fungus type was determined by microscopic analysis. The main finding was that spruce heartwood had fewer and shorter cracks and less surface-discolouring fungus growth than sapwood. This was valid for both painted and untreated wood. After 2 years’ exposure, the cracks in sapwood (upper surface) were more than three times longer and about five times more numerous than in heartwood for both painted and untreated boards. Microscopic study showed that surface discoloration was due mainly to Aureobasidium pullulans, together with a few other discolouring fungi. After 5.5 years, initial decay was established on the surface and in the end grain of four untreated test objects.Keywords
This publication has 18 references indexed in Scilit:
- Crack formation due to weathering of radial and tangential sections of pine and spruceWood Material Science & Engineering, 2006
- Testing and evaluation of natural durability of wood in above ground conditions in Europe – an overviewJournal of Wood Science, 2005
- Comparative study on penetration characteristics of modern wood coatingsWood Science and Technology, 1998
- Increase in the content of low-molecular carbohydrates at lumber surfaces during drying and correlations with nitrogen content, yellowing and mould growthWood Science and Technology, 1993
- The Influence of Drying Schedules on the Redistribution of Low-Molecular Sugars inPinus sylvestrisL.Holzforschung, 1993
- The effect of aging on the ultrastructure of woodWood Science and Technology, 1975
- Untersuchungen an bewitterten Holzoberflächen—Zweite Mitteilung: Verwitterungserscheinungen an ungeschützten HölzernEuropean Journal of Wood and Wood Products, 1971
- Zum Resistenzverhalten von Holz bei natürlicher BewitterungEuropean Journal of Wood and Wood Products, 1969
- The Chemistry of Colour Changes in Wood I. The Significance of StilbenesHolzforschung, 1968
- Natural Resistance of Wood to Microbial DeteriorationAnnual Review of Phytopathology, 1966