Lithium adsorption on MgO(100) and its defects: Charge transfer, structure, and energetics
- 15 July 2009
- journal article
- research article
- Published by American Physical Society (APS) in Physical Review B
- Vol. 80 (3), 035418
- https://doi.org/10.1103/physrevb.80.035418
Abstract
The adsorption energetics and growth of lithium vapor on MgO(100) at 300 K was studied using microcalorimetry, in combination with low-energy electron diffraction (LEED), low-energy ion scattering (ISS), Auger electron spectroscopy (AES), and work-function measurements. The MgO(100) samples were films of thickness grown on a Mo(100) single crystal. The initial sticking probability of lithium was , reaching unity by 0.5 monolayer (ML). The AES and ISS signals vary with Li coverage up to 3 ML as expected if the Li atoms stay within the layer where they initially hit (i.e., with no interlayer transport). Initially, lithium adsorbs strongly at the intrinsic surface defects and as two-dimensional (2D) lithium clusters, with a heat of adsorption of 260 kJ/mol. The heat approaches the heat of sublimation of bulk Li (159 kJ/mol) by 0.4 ML, due to the growth of 2D and then three-dimensional (3D) Li islands. Argon-ion sputtering of the surface increases the defect density and the probability for adsorbing Li to find a defect, and thus the heat of adsorption at low coverages. When defects only are being populated, Li exhibits a heat of adsorption of 410 kJ/mol. Comparing heats with recent density functional theory (DFT) calculations suggests that the defect sites are under-coordinated O atoms at steps or kinks, or related structures at dislocations. The work function decreases by within the first 0.5 ML and then increases to near the value of bulk Li(solid), , by 3 ML. These results support recent DFT calculations predicting stronger electron transfer from Li to the MgO when at steps and kinks than at terraces, and decreasing charge transfer as 2D Li clusters grow. The work function starts to increase when the growth mode becomes dominated by growth of 3D Li(solid). In spite of a large amount of electron transfer from Li to MgO, Li adatoms have attractive interactions that lead to 2D clustering. For 1-nm-thick MgO films, the heat of adsorption was higher by 60–20 kJ/mol than for 4 nm films in the entire range from 0 to 0.7 ML, where adsorption in the first layer dominates.
Keywords
This publication has 61 references indexed in Scilit:
- Interaction of Gold Clusters with Color Centers on MgO(001) FilmsAngewandte Chemie-International Edition, 2006
- Li-induced metal-semiconductor-metal transitions on thesurface: A work function, photoemission, and NMR studyPhysical Review B, 2005
- Structure of ultrathin MgO films on Mo(001)Thin Solid Films, 2003
- Interaction of Ag with MgO(100)The Journal of Physical Chemistry B, 2002
- Metal films and particles on oxide surfaces: structural, electronic and chemisorptive propertiesJournal of the Chemical Society, Faraday Transactions, 1996
- Surface colour centres on magnesium oxide generated by magnesium and alkali-metal dopingJournal of the Chemical Society, Faraday Transactions, 1994
- A novel lithium ionic cluster at the surface of magnesiaThe Journal of Physical Chemistry, 1993
- Electron-energy-loss-spectroscopy studies of thermally generated defects in pure and lithium-doped MgO(100) films on Mo(100)Physical Review B, 1992
- A possible solution to the problem of compositional change with ion‐bombarded oxidesSurface and Interface Analysis, 1992
- The Work Function of LithiumPhysical Review B, 1949