Micromechanical Modeling of Fatigue Crack Nucleation around Non-Metallic Inclusions in Martensitic High-Strength Steels
Open Access
- 24 November 2019
- Vol. 9 (12), 1258
- https://doi.org/10.3390/met9121258
Abstract
Martensitic high-strength steels are prone to exhibit premature fatigue failure due to fatigue crack nucleation at non-metallic inclusions and other microstructural defects. This study investigates the fatigue crack nucleation behavior of the martensitic steel SAE 4150 at different microstructural defects by means of micromechanical simulations. Inclusion statistics based on experimental data serve as a reference for the identification of failure-relevant inclusions and defects for the material of interest. A comprehensive numerical design of experiment was performed to systematically assess the influencing parameters of the microstructural defects with respect to their fatigue crack nucleation potential. In particular, the effects of defect type, inclusion–matrix interface configuration, defect size, defect shape and defect alignment to loading axis on fatigue damage behavior were studied and discussed in detail. To account for the evolution of residual stresses around inclusions due to previous heat treatments of the material, an elasto-plastic extension of the micromechanical model is proposed. The non-local Fatemi–Socie parameter was used in this study to quantify the fatigue crack nucleation potential. The numerical results of the study exhibit a loading level-dependent damage potential of the different inclusion–matrix configurations and a fundamental influence of the alignment of specific defect types to the loading axis. These results illustrate that the micromechanical model can quantitatively evaluate the different defects, which can make a valuable contribution to the comparison of different material grades in the future.Keywords
This publication has 65 references indexed in Scilit:
- Effect of impurity level and inclusions on the ductility and toughness of an ultra-high-strength steelMaterials Science and Engineering: A, 2017
- Influence of non-metallic inclusions on fatigue life in the very high cycle fatigue regimeInternational Journal of Fatigue, 2016
- The Effects of Sulfide Inclusions on Mechanical Properties and Failures of Steel ComponentsJournal of Failure Analysis and Prevention, 2015
- Vehicle lightweighting vs. electrification: Life cycle energy and GHG emissions results for diverse powertrain vehiclesApplied Energy, 2014
- Nichtmetallische Einschlüsse in Langprodukten Entstehung, Bestimmung, Auswirkungen – ein ÜberblickBHM Berg- und Hüttenmännische Monatshefte, 2009
- Effects of Sulfur Level and Anisotropy of Sulfide Inclusions on Tensile, Impact, and Fatigue Properties of SAE 4140 SteelSAE International Journal of Materials and Manufacturing, 2008
- An In-Situ Scanning Electron Microscopy Study of the Bonding between MnS Inclusions and the Matrix during Tensile Deformation of Hot-Rolled SteelsMetallurgical and Materials Transactions A, 2007
- Fatigue anisotropy in cross-rolled, hardened medium carbon steel resulting from MnS inclusionsMetallurgical and Materials Transactions A, 2006
- On the critical inclusion size of high strength steels under ultra-high cycle fatigueMaterials Science and Engineering: A, 2006
- A theory of fatigue crack initiation at inclusionsMetallurgical Transactions A, 1982