Nickel selenide as a high-efficiency catalyst for oxygen evolution reaction
Top Cited Papers
- 26 November 2015
- journal article
- research article
- Published by Royal Society of Chemistry (RSC) in Energy & Environmental Science
- Vol. 9 (5), 1771-1782
- https://doi.org/10.1039/c5ee02463c
Abstract
A metal-rich form of Ni-selenide, nickel subselenide, Ni3Se2 has been investigated as a potential oxygen evolution electrocatalyst under alkaline conditions for the first time. The Ni3Se2 phase has a structure similar to the sulfur mineral heazlewoodite, which contains metal–metal bonding. The electrocatalytic activities of Ni3Se2 towards OER were seen to be at par with or even superior to the transition metal oxide based electrocatalyst in terms of onset overpotential for O2 evolution as well as overpotential to reach a current density of 10 mA cm−2 (observed at 290 mV). The electrocatalytic Ni3Se2 films were grown by electrodeposition on conducting substrates and the deposition parameters including the pH of the electrolytic bath, deposition potential, and substrate composition were seen to have some influence on the catalytic activity. So far, Ni3Se2 films deposited on the Au-coated Si substrate was seen to have the lowest overpotential. Annealing of the as-deposited electrocatalytic films in an inert atmosphere, enhanced their catalytic efficiencies by decreasing the overpotential (@10 mA cm−2) as well as increasing the current density. The structure and morphology of these films has been characterized by powder X-ray diffraction, scanning and transmission electron microscopy, Raman, and X-ray photoelectron spectroscopy. Catalytic activities were investigated through detailed electrochemical studies under alkaline conditions, including linear sweep voltammetry, chronoamperometric studies at constant potential, electrochemical surface area determination and calculation of the Tafel slope. The Faradaic efficiency of this catalyst has been estimated by reducing the evolved O2 in a RRDE set-up which also confirmed that the evolved gas was indeed O2. In addition to low overpotentials, these Ni3Se2 electrodeposited films were seen to be exceptionally stable under conditions of continuous O2 evolution for an extended period (42 h).Keywords
Funding Information
- American Chemical Society Petroleum Research Fund (54793-ND10)
This publication has 66 references indexed in Scilit:
- Colloidal Iron Pyrite (FeS2) Nanocrystal Inks for Thin-Film PhotovoltaicsJournal of the American Chemical Society, 2010
- Hierarchical Hollow Co9S8 Microspheres: Solvothermal Synthesis, Magnetic, Electrochemical, and Electrocatalytic PropertiesChemistry – A European Journal, 2010
- NixCo3−xO4 Nanowire Arrays for Electrocatalytic Oxygen EvolutionAdvanced Materials, 2010
- Carbon-supported Co1.67Te2 nanoparticles as electrocatalysts for oxygen reduction reaction in alkaline electrolyteJournal of Materials Chemistry, 2009
- Superconductivity in the PbO-type structure α-FeSeProceedings of the National Academy of Sciences of the United States of America, 2008
- Don't Forget Long-Term Fundamental Research in EnergyScience, 2007
- Powering the planet: Chemical challenges in solar energy utilizationProceedings of the National Academy of Sciences of the United States of America, 2006
- Co9S8as a Catalyst for Electroreduction of O2: Quantum Chemistry PredictionsThe Journal of Physical Chemistry B, 2005
- Electron Density Distributions Calculated for the Nickel Sulfides Millerite, Vaesite, and Heazlewoodite and Nickel Metal: A Case for the Importance of Ni−Ni Bond Paths for Electron TransportThe Journal of Physical Chemistry B, 2005
- Structure of hazelwoodite (Ni3S2)Acta Crystallographica Section B: Structural Science, Crystal Engineering and Materials, 1980