Nanoscale Hydrophobic Recovery: A Chemical Force Microscopy Study of UV/Ozone-Treated Cross-Linked Poly(dimethylsiloxane)
- 30 December 2003
- journal article
- research article
- Published by American Chemical Society (ACS) in Langmuir
- Vol. 20 (3), 785-794
- https://doi.org/10.1021/la035552k
Abstract
Chemical force microscopy (CFM) in water was used to map the surface hydrophobicity of UV/ozone-treated poly(dimethylsiloxane) (PDMS; Sylgard 184) as a function of the storage/recovery time. In addition to CFM pull-off force mapping, we applied indentation mapping to probe the changes in the normalized modulus. These experiments were complemented by results on surface properties assessed on the micrometer scale by X-ray photoelectron spectroscopy and water contact-angle measurements. Exposure times of ≤30 min resulted in laterally homogeneously oxidized surfaces, which are characterized by an increased modulus and a high segmental mobility of PDMS. As detected on a sub-50-nm level, the subsequent “hydrophobic recovery” was characterized by a gradual increase in the pull-off forces and a decrease in the normalized modulus, approaching the values of unexposed PDMS after 8−50 days. Lateral imaging on briefly exposed PDMS showed the appearance of liquid PDMS in the form of droplets with an increasing recovery time. Longer exposure times (60 min) led to the formation of a hydrophilic silica-like surface layer. Under these conditions, a gradual surface reconstruction within the silica-like layer occurred with time after exposure, where a hydrophilic SiOx-enriched phase formed <100-nm-sized domains, surrounded by a more hydrophobic matrix with lower normalized modulus. These results provide new insights into the lateral homogeneity of oxidized PDMS with a resolution in the sub-50-nm range.Keywords
This publication has 65 references indexed in Scilit:
- Investigation of the stiffness change in, the indentation force and the hydrophobic recovery of plasma-oxidized polydimethylsiloxane surfaces by tapping mode atomic force microscopyPolymer, 2001
- Mapping the Surface Heterogeneity of a Polymer Blend: An Adhesion-Force-Distribution Study Using the Atomic Force MicroscopeLangmuir, 2000
- UV–ozone induced growth of a SiOx surface layer on a cross-linked polysiloxane film: characterization and gas separation propertiesJournal of Membrane Science, 2000
- Toward High Resolution Mapping of Functional Group Distributions at Surface-Treated Polymers by AFM Using Modified TipsMacromolecules, 2000
- Atomic Force Microscopy of Elastomers: Morphology, Distribution of Filler Particles, and Adhesion Using Chemically Modified TipsRubber Chemistry and Technology, 1999
- Organic and Inorganic Contamination on Commercial AFM CantileversLangmuir, 1999
- Rapid Prototyping of Microfluidic Systems in Poly(dimethylsiloxane)Analytical Chemistry, 1998
- Improvement of the micro-wear resistance of silicone by vacuum ultraviolet irradiationPolymer, 1998
- CHEMICAL FORCE MICROSCOPYAnnual Review of Materials Science, 1997
- The Surface Activity of Silicones: A Short ReviewIndustrial & Engineering Chemistry Product Research and Development, 1980