Comparison of UV-degradation depth-profiles in polyethylene, polypropylene and an ethylene–propylene copolymer
- 30 June 2005
- journal article
- Published by Elsevier BV in Polymer Degradation and Stability
- Vol. 88 (3), 415-419
- https://doi.org/10.1016/j.polymdegradstab.2004.12.006
Abstract
No abstract availableKeywords
This publication has 29 references indexed in Scilit:
- Depth profile analysis of the photochemical degradation of polycarbonate by infrared spectroscopyPolymer Degradation and Stability, 2003
- Degradation profile of polyethylene after artificial accelerated weatheringPolymer Degradation and Stability, 2003
- Submicrometric characterization of the heterogeneous photooxidation of polypropylene by microthermal analysisPolymer Degradation and Stability, 2002
- Depth-profile of photo-oxidation of polyoctenamerPolymer Degradation and Stability, 2002
- Improvement of the mechanical properties of photo-oxidized films after recyclingPolymer Degradation and Stability, 2002
- A general solution of the closed-loop kinetic scheme for the thermal oxidation of polypropylenePolymer Degradation and Stability, 2001
- Degradation depth profiles and fracture of UV exposed polycarbonatePlastics, Rubber and Composites: Macromolecular Engineering, 2001
- Thermal oxidation of hydroxyl-terminated polybutadiene rubber II. Oxidation depth profiles studied by imaging chemiluminescencePolymer Degradation and Stability, 1999
- Hydroperoxide formation in irradiated polyethyleneJournal of Polymer Science Part A: Polymer Chemistry, 1999
- Molecular weight changes during the photooxidation of isotactic polypropylenePolymer Degradation and Stability, 1996