Micromachining in plastics using X-ray lithography for the fabrication of microelectrophoresis devices.

Abstract
Micromachining was performed in polymethylmethacrylate (PMMA) using X-ray lithography for the fabrication of miniaturized devices (microchips) for potential applications in chemical and genetic analyses. The devices were fabricated using two different techniques: transfer mask technology and a Kapton mask. For both processes, the channel topography was transferred (1:1) to the appropriate substrate via the use of an optical mask. In the case of the transfer mask technique, the PMMA substrate was coated with a positive photoresist and a thin Au/Cr plating base. Following UV exposure, the resist was developed and a thick overlayer (approximately 3 microns) of Au electroplated onto the PMMA substrate only where the resist was removed, which acted as an absorber of the X-rays. In the other technique, a Kapton film was used as the X-ray mask. In this case, the Kapton film was UV exposed using the optical mask to define the channel topography and following development of the resist, a thick Au overlayer (8 microns) was electrodeposited onto the Kapton sheet. The PMMA wafer during X-ray exposure was situated directly underneath the Kapton mask. In both cases, the PMMA wafer was exposed to soft X-rays and developed to remove the exposed PMMA. The resulting channels were found to be 20 microns in width (determined by optical mask) with channel depths of approximately 50 microns (determined by x-ray exposure time). In order to demonstrate the utility of this micromachining process, several components were fabricated in PMMA including capillary/chip connectors, injectors for fixed-volume sample introduction, separation channels for electrophoresis and integrated fiber optic fluorescence detectors. These components could be integrated into a single device to assemble a system appropriate for the rapid analysis of various targets.