Asymmetric cryorolling for fabrication of nanostructural aluminum sheets
Open Access
- 24 October 2012
- journal article
- research article
- Published by Springer Science and Business Media LLC in Scientific Reports
- Vol. 2 (1), 772
- https://doi.org/10.1038/srep00772
Abstract
Nanostructural Al 1050 sheets were produced using a novel method of asymmetric cryorolling under ratios of upper and down rolling velocities (RUDV) of 1.1, 1.2, 1.3, and 1.4. Sheets were rolled to about 0.17 mm from 1.5 mm. Both the strength and ductility of Al 1050 sheets increase with RUDVs. Tensile strength of Al sheets with the RUDV 1.4 is larger 22.3% of that for RUDV 1.1, which is 196 MPa. The TEM observations show the grain size is 360 nm when the RUDV is 1.1, and 211 nm for RUDV 1.4.Keywords
This publication has 34 references indexed in Scilit:
- SEM EBSD and TEM Structure Studies of α-Brass after Severe Plastic Deformation Using Equal Channel Rolling Followed by Groove PressingSolid State Phenomena, 2012
- A theoretical and experimental evaluation of repetitive corrugation and straightening: Application to Al–Cu and Al–Cu–Sc alloysMaterials Science and Engineering: A, 2012
- Effects of ARB and ageing processes on mechanical properties and microstructure of 6061 aluminum alloyJournal of the American Academy of Dermatology, 2011
- Microstructural evolution in an Al-6061 alloy processed by high-pressure torsionMaterials Science and Engineering: A, 2010
- Development of severe plastic deformation by various asymmetric rolling processesMaterials Science and Engineering: A, 2009
- Development of Mg–6.0%Zn–1.0%Y–0.6%Ce–0.6%Zr magnesium alloy and its microstructural evolution during processingMaterials Science and Engineering: A, 2008
- The theoretical and experimental analysis of the effect of asymmetrical rolling on the value of unit pressureJournal of the American Academy of Dermatology, 2004
- Numerical and experimental investigations of constrained groove pressing and rolling for grain refinementJournal of the American Academy of Dermatology, 2002
- Microstructures and mechanical properties of 6061 aluminum alloy processed by accumulative roll-bondingMaterials Science and Engineering: A, 2002
- Effect of aging treatment on heavily deformed microstructure of a 6061 aluminum alloy after equal channel angular pressingScripta Materialia, 2001