Effect of Surface Treatment of Halloysite Nanotubes (HNTs) on the Kinetics of Epoxy Resin Cure with Amines
Open Access
- 16 April 2020
- Vol. 12 (4), 930
- https://doi.org/10.3390/polym12040930
Abstract
The epoxy/clay nanocomposites have been extensively considered over years because of their low cost and excellent performance. Halloysite nanotubes (HNTs) are unique 1D natural nanofillers with a hollow tubular shape and high aspect ratio. To tackle poor dispersion of the pristine halloysite (P-HNT) in the epoxy matrix, alkali surface-treated HNT (A-HNT) and epoxy silane functionalized HNT (F-HNT) were developed and cured with epoxy resin. Nonisothermal differential scanning calorimetry (DSC) analyses were performed on epoxy nanocomposites containing 0.1 wt.% of P-HNT, A-HNT, and F-HNT. Quantitative analysis of the cure kinetics of epoxy/amine system made by isoconversional Kissinger–Akahira–Sunose (KAS) and Friedman methods made possible calculation of the activation energy (Eα) as a function of conversion (α). The activation energy gradually increased by increasing α due to the diffusion-control mechanism. However, the average value of Eα for nanocomposites was lower comparably, suggesting autocatalytic curing mechanism. Detailed assessment revealed that autocatalytic reaction degree, m increased at low heating rate from 0.107 for neat epoxy/amine system to 0.908 and 0.24 for epoxy/P-HNT and epoxy/A-HNT nanocomposites, respectively, whereas epoxy/F-HNT system had m value of 0.072 as a signature of dominance of non-catalytic reactions. At high heating rates, a similar behavior but not that significant was observed due to the accelerated gelation in the system. In fact, by the introduction of nanotubes the mobility of curing moieties decreased resulting in some deviation of experimental cure rate values from the predicted values obtained using KAS and Friedman methods.This publication has 47 references indexed in Scilit:
- Curing epoxy with polyvinylpyrrolidone (PVP) surface-functionalized Mn Fe3-O4 magnetic nanoparticlesProgress in Organic Coatings, 2019
- Curing epoxy with electrochemically synthesized Mn Fe3-O4 magnetic nanoparticlesProgress in Organic Coatings, 2019
- Thin films of epoxy adhesives containing recycled polymers and graphene oxide nanoflakes for metal/polymer composite interfaceProgress in Organic Coatings, 2019
- Curing epoxy with polyvinyl chloride (PVC) surface-functionalized CoxFe3-xO4 nanoparticlesProgress in Organic Coatings, 2019
- Curing epoxy with electrochemically synthesized Co Fe3-O4 magnetic nanoparticlesProgress in Organic Coatings, 2019
- Curing epoxy with polyethylene glycol (PEG) surface-functionalized Gd Fe3-O4 magnetic nanoparticlesProgress in Organic Coatings, 2019
- Cure Index demonstrates curing of epoxy composites containing silica nanoparticles of variable morphology and porosityProgress in Organic Coatings, 2019
- Multi-nationality epoxy adhesives on trial for future nanocomposite developmentsProgress in Organic Coatings, 2019
- Properties of nano-Fe3O4 incorporated epoxy coatings from Cure Index perspectiveProgress in Organic Coatings, 2019
- Shape and size effects of ceria nanoparticles on the impact strength of ceria/epoxy resin compositesParticuology, 2011