The Structural and Mechanical Properties of MoS2-TiB2 Coated on AA7075 Produced by Powder Metallurgy Method
- 17 December 2019
- journal article
- Published by ACADEMY Saglik Hiz. Muh. Ins. Taah. Elekt. Yay. Tic. Ltd. Sti. in Journal of Brilliant Engineering
- Vol. 1 (2), 11-14
- https://doi.org/10.36937/ben.2020.002.004
Abstract
AA7075 Al alloys are widely used in the aerospace industry. However, the mechanical properties of these alloys are insufficient in space conditions. AA7075 Al alloy is produced by powder metallurgy method due to the good wear properties. Then AA7075 Al alloys have to be adapted to mechanical properties MoS2-TiB2 composite films are deposited. MoS2-TiB2 composite films were grown on powder metal substrate using CFUBMS method in three different MoS2 target currents. Structural properties of composite films were analyzed by SEM, XRD and XPS methods. The mechanical properties of the films are carried out by microhardness and scratch tester. The best grade value of AA7075 powder metal alloy was made with 800MPa pressing pressure and increased from 2.61g/cm3 to 2.72g/cm3 after sintering. The highest hardness was obtained at the lowest MoS2 target voltage of 4.7GPa. The highest critical load value was obtained as 26N at the highest MoS2 target voltage.Keywords
This publication has 19 references indexed in Scilit:
- Mechanical properties of aluminum 7075 – Silver nanoparticles powder composite and its relationship with the powder particle sizeAdvanced Powder Technology, 2016
- Effect of Compaction Load and Sintering Temperature on Tribological and Mechanical Behavior of Ni/SiC/MoS2 CompositesJournal of Materials Engineering and Performance, 2016
- Microstructure and pitting corrosion of armor grade AA7075 aluminum alloy friction stir weld nugget zone – Effect of post weld heat treatment and addition of boron carbideDefence Technology, 2015
- Investigation of the friction and wear properties of Ti/TiB 2 /MoS 2 graded-composite coatings deposited by CFUBMS under air and vacuum conditionsSurface and Coatings Technology, 2014
- Deformation of powder metallurgy materials in cold and hot formingJournal of the American Academy of Dermatology, 2008
- Microstructure and mechanical properties of MoS2/titanium composite coatings with different titanium contentSurface and Coatings Technology, 2007
- Co-sputtered Mo:S:C:Ti:B based coating for tribological applicationsSurface and Coatings Technology, 2005
- Effect of crystallographic orientation on the friction and wear properties of MoxSy–Ti coatings by pulsed-dc in nitrogen and humid airWear, 2005
- Metal incorporation in sputter-deposited MoS2 films studied by extended x-ray absorption fine structureJournal of Materials Research, 1995
- Lubrication with sputtered MoS2 films: Principles,operation, and limitationsJournal of Materials Engineering and Performance, 1992