Ultrafine Spheroidal Graphite Iron Castings
- 1 January 2019
- journal article
- research article
- Published by Japan Institute of Metals in MATERIALS TRANSACTIONS
- Vol. 60 (1), 41-48
- https://doi.org/10.2320/matertrans.mg201810
Abstract
Gravity die casting of spheroidal graphite iron had been attempted controlling free nitrogen during preparing base molten iron, magnesium treatment, inoculation and pouring. In this study, the actual CO/SiO2 reaction temperature of base molten irons was surveyed and magnesium treatment was conducted at that temperature. The mold was made of steel and the cavity size was thickness of 5.4mm and diameter of 35 mm. As the results, ultrafine graphite nodules were obtained without chill in as-cast condition. They were average diameter of 7 mu m and density count of over 3,000/mm(2). Knuckle for automobile was also cast taking the same procedure. Knuckle had no meager defect like shrinkage, chill etc. in as-cast conditions. The possibility of no chill has become extremely higher than former study.Keywords
This publication has 6 references indexed in Scilit:
- Fabricación de piezas de fundición con grafito esferoidal en molde metálicoRevista de Metalurgia, 2013
- Study of voids in chilled samples of magnesium treated ironsInternational Journal of Cast Metals Research, 2004
- The influence of free magnesium on some properties in spheroidal graphite ironsInternational Journal of Cast Metals Research, 1999
- Studies on the Rate of Absorption of Nitrogen in Liquid Iron Containing Surface Active ElementsTetsu-to-Hagane, 1968
- The Diplomatic History of British Honduras, 1638-1901Hispanic American Historical Review, 1962
- STUDY ON ALLOY CHILLED ROLLSTetsu-to-Hagane, 1932