On the loading rate dependence of environment-assisted cracking in sensitized AA5456-H116 exposed to marine environments
- 26 March 2022
- journal article
- research article
- Published by Elsevier BV in Corrosion Science
- Vol. 201, 110267
- https://doi.org/10.1016/j.corsci.2022.110267
Abstract
No abstract availableKeywords
Funding Information
- NASA Engineering and Safety Center (80NSSC21P0569)
- National Aeronautics and Space Administration
This publication has 75 references indexed in Scilit:
- Simulation of hydrogen assisted stress corrosion cracking using the cohesive modelEngineering Fracture Mechanics, 2008
- Emerging Issues and Fundamental Processes in Environmental Cracking in Hot WaterCorrosion, 2008
- Stress Corrosion Cracking of Al-Mg and Mg-Al AlloysCorrosion, 2004
- Crack-particle interactions during intergranular stress corrosion of AA5083 as observed by cross-section transmission electron microscopyScripta Materialia, 2004
- EFFECT OF DISPLACEMENT RATES ON EAC OF AISI 4340 STEELFatigue & Fracture of Engineering Materials & Structures, 1998
- Limitations of the Slow Strain Rate Test for Stress Corrosion Cracking TestingCorrosion, 1992
- APPLICATION OF FRACTURE MECHANICS TECHNIQUES TO THE ENVIRONMENTALLY ASSISTED CRACKING OF ALUMINIUM 2024Fatigue & Fracture of Engineering Materials & Structures, 1989
- Slow Strain Rate Testing for Materials Evaluation in High-Pressure H2S EnvironmentsCorrosion, 1988
- Determination of Threshold Stress Corrosion Cracking Characteristics Using Rising LoadKIscc Testing Based on Ultrasonic MethodJournal of Testing and Evaluation, 1985
- On the relationship between critical tensile stress and fracture toughness in mild steelJournal of the Mechanics and Physics of Solids, 1973