Mechanical degradation due to vacancies produced by grain boundary corrosion of steel
- 1 November 2020
- journal article
- research article
- Published by Elsevier BV in Acta Materialia
- Vol. 200, 471-480
- https://doi.org/10.1016/j.actamat.2020.08.080
Abstract
No abstract availableKeywords
Funding Information
- National Centre for Supercomputing Applications
- National Science Foundation of Sri Lanka
- U.S. Department of Transportation
This publication has 61 references indexed in Scilit:
- Coarse-grained atomistic simulation of dislocationsJournal of the Mechanics and Physics of Solids, 2011
- Atomistic simulations of nanoindentation in the presence of vacanciesScripta Materialia, 2010
- Interatomic potentials for hydrogen in–iron based on density functional theoryPhysical Review B, 2009
- Atomistic study of hydrogen distribution and diffusion around a {1 1 2} edge dislocation in alpha ironActa Materialia, 2008
- Computer simulation of interaction of an edge dislocation with a carbon interstitial in α-iron and effects on glideActa Materialia, 2007
- Surface roughness effects on the displacement bursts observed in nanoindentationJournal of Materials Research, 2004
- Thin-film fracture during nanoindentation of a titanium oxide film–titanium systemJournal of Materials Research, 2001
- The Use of Percolation Theory to Predict the Probability of Failure of Sensitized, Austenitic Stainless Steels by Intergranular Stress Corrosion CrackingCorrosion, 1989
- The effects of film formation and mechanical factors on the initiation of stress corrosion cracking of unalloyed steels in carbonate solutionsMaterials and Corrosion, 1980
- Defect trapping of ion-implanted deuterium in FeJournal of Applied Physics, 1979