Alloying of U-Al-SS as a Simulant for Pu-Al-SS Alloying
- 11 November 2021
- journal article
- research article
- Published by Taylor & Francis Ltd in Nuclear Technology
- Vol. 208 (6), 1049-1058
- https://doi.org/10.1080/00295450.2021.1988821
Abstract
The Savannah River National Laboratory evaluated several options for disposition of stainless steel (SS)–clad plutonium metal, particularly Pu-10.6 at. % Al (Pu- 1.3 wt% Al) alloy fuel. One technology considered was alloying fuel with SS. The goal of the alloying would be to make a SS-Pu alloy that was a nonproliferable waste form with secondary Pu-rich microencapsulated regions distributed throughout the refractory SS. The microencapsulation of the Pu regions should therefore allow the waste form to meet the requirements for a low attractiveness waste as defined by the U.S. Department of Energy. Plutonium-bearing alloys at these levels could potentially be suitable for disposal at a waste isolation pilot plant. Four metal ingots were successfully fabricated using U and Al as a surrogate for Pu-Al. The U was distributed and microencapsulated by the alloy matrix, thereby setting the stage for subsequent tests using SS-clad fuel elements containing Pu-10.6Al.Keywords
This publication has 9 references indexed in Scilit:
- Microstructure evolution in AISI 304 stainless steel during near rapid directional solidificationMaterials Science and Technology, 2009
- Effect of cooling rate on solidification microstructures in AISI 304 stainless steelMaterials Science and Technology, 2008
- Host phases for actinides in simulated metallic waste formsJournal of Nuclear Materials, 2003
- Characteristics of the Melt-Dilute Form of Aluminum-Based Nuclear Spent FuelPublished by Office of Scientific and Technical Information (OSTI) ,2002
- Actinide distribution in a stainless steel–15 wt% zirconium high-level nuclear waste formJournal of Nuclear Materials, 2000
- Evaluation of stainless steel–zirconium alloys as high-level nuclear waste formsJournal of Nuclear Materials, 1998
- Laves intermetallics in stainless steel–zirconium alloysMaterials Science and Engineering: A, 1997
- Effective interdiffusion coefficients and penetration depthsScripta Metallurgica et Materialia, 1991
- Diffusion of Chromium, Manganese, and Nickel in Molten IronTransactions of the Japan Institute of Metals, 1975